The present invention discloses a kind of anti-stretching lightweight and environmental friendly cement-based artificial stone material and its preparation process, including the following raw materials: white cement 40 60 parts, hydroxylated fly ash 30 50 parts, slag 15 25 parts, river sand 10 20 parts, gravel 25 40 parts, waste tire powder 10 15 parts, methacrylic monomer 10 15 parts, carboxyl-terminated liquid nitrile butadiene rubber 15 20 parts, initiator 0.5 1 part. Catalyst 0.5 1, urea 5 15, activator 10 15, silane coupling agent 1 3, water 60 70; hydroxylated fly ash is prepared by hydrothermal reaction of fly ash with sodium hydroxide solution and re-acidification; the activator is composed of sodium peroxide, calcium oxide and zinc sulfate at a mass ratio of 2:5:1. The cement-based artificial stone has the advantages of light material, good toughness, high tensile strength, excellent thermal insulation performance and easy construction.
【技术实现步骤摘要】
抗拉伸轻质环保型水泥基人造石材及其制备工艺
本专利技术属于建筑材料
，具体涉及一种抗拉伸轻质环保型水泥基人造石材及其制备工艺。
技术介绍
水泥基人造石材是以各种水泥为胶结材料，以天然碎石粒、砂为粗细骨料，经配制、搅拌、加压蒸养、磨光和抛光后制成的人造石材，原料来源广、取材方便、成本低廉，但是其脆性高，韧性差，抗拉伸强度低，且成型人造石材密度较高，过于笨重，加大施工难度。粉煤灰是从燃煤电厂以及煤矸石、煤泥资源综合利用电厂锅炉烟气中收捕的细灰和炉底渣，平均每消耗2吨煤会产生1吨粉煤灰，主要氧化物组成为：SiO2、Al2O3、FeO、Fe2O3、CaO、TiO2等。随着电力工业的发展，燃煤电厂的粉煤灰排放量逐年增加，成为我国当前排量较大的工业废渣之一，粉煤灰的大量堆积不仅造成土地资源的浪费，其中有毒化学物质还会危害人类健康、污染环境。利用粉煤灰代替部分水泥生产人造石材，不仅实现了粉煤灰的资源化开发利用，变废为宝，节约生产成本，降低环境污染，还提高水泥的和易性和可泵性及粉煤灰的附加价值。因此，如何利用粉煤灰生产出一种轻质、高韧性、抗拉伸的环保型水泥基人造石材是亟待解...
【技术保护点】
1.一种抗拉伸轻质环保型水泥基人造石材，其特征在于，包括以下重量份原料：
【技术特征摘要】
1.一种抗拉伸轻质环保型水泥基人造石材，其特征在于，包括以下重量份原料：所述羟基化粉煤灰的制备方法如下：将粉煤灰加入3.5mol/L氢氧化钠溶液中，在超声波辅助下，120-160℃水热反应6h,过滤后，水洗至PH降为7-8，加入混合酸溶液中，混合酸溶液由1mol/L硝酸溶液和2mol/L硫酸溶液按1：3的体积比混合而成，65-80℃搅拌反应6h，过滤、洗涤、真空冷冻干燥，即得羟基化粉煤灰；所述激活剂由过氧化钠、氧化钙、硫酸锌按2：5：1的质量比混合而成。2.根据权利要求1所述一种抗拉伸轻质环保型水泥基人造石材，其特征在于，所述碎石粒径介于5-8mm。3.根据权利要求1所述一种抗拉伸轻质环保型水泥基人造石材，其特征在于，所述引发剂包括过硫酸钾、过硫酸铵、偶氮二异丁腈中的一种或多种。4.根据权利要求1所述一种...
【专利技术属性】
技术研发人员：吴天保，
申请(专利权)人：安徽米方石材有限公司，
类型：发明
国别省市：安徽,34