The invention discloses a method for preparing a thermally induced irreversible composite hydrogel with antibacterial and promoting wound healing function and its application. After dissolving the gel into silver loaded graphene solution, the gel is sprayed on the wound surface and forms an irreversible hydrogel through stimulation of the wound surface temperature. The thermosensitive hydrogel provided by the invention has the advantages of simple preparation method, anti-bacterial and wound healing promoting functions, and is used as wound dressing with obvious effect and great clinical application potential.
【技术实现步骤摘要】
一种具有抗菌和促进伤口愈合功能的热诱导不可逆复合水凝胶的制备方法及其应用
本专利技术涉及一种具有抗菌和促进伤口愈合功能的热诱导不可逆复合水凝胶的制备方法及其应用。
技术介绍
水凝胶是一种新型的伤口敷料材料，是由良好的生物相容性和生物可降解性的聚合物制成的一种三维交联多孔材料。水凝胶含有大量的水，具有可调控的机械性能，可以很容易地注射或喷涂在伤口表面，与伤口缝合线和胶带等常规伤口治疗方法相比，水凝胶可以快速粘附在伤口表面，减少缝合区出血，预防术后并发症，促进伤口愈合。以此为基础，水凝胶材料在抗菌和创伤类伤口敷料的应用引起了研究者的关注，并且一些水凝胶伤口敷料已得到商业化的应用，如BioGlue(医用软组织粘合剂)、DuraSealTM(CongluentSurgical公司)、CoSealTM(外科用封合剂)等。水凝胶的形成机制主要是化学交联和物理交联。化学交联水凝胶是基质材料在外加交联剂或催化剂的作用下形成稳定的共价键构建高度交联结构形成的水凝胶，具有永久稳定性、良好的附着力和机械性能，但缺点也非常明显：交联剂需要单独储存并在形成水凝胶之前加入到基质中，若交联剂在...
【技术保护点】
1.一种具有抗菌和促进伤口愈合功能的热诱导不可逆复合水凝胶的制备方法，其特征在于包括如下步骤：步骤1：取10～30g聚乙二醇和1～5g三乙胺溶解在二氯甲烷中，通入氩气保护后，加入2～8g 2‑溴代异丁酰溴，将溶液在0℃下搅拌1小时，然后在室温下再搅拌24～72小时，所得产物经铝柱分离、透析、冻干后，获得原子转移自由基聚合引发剂；步骤2：将步骤1获得的所述原子转移自由基聚合引发剂取0.1～0.5g溶解在异丙醇/水混合溶剂中，放入至聚合瓶，然后加入1～10g温敏性单体、0.1～0.5g疏水性单体、10～50mg氯化亚铜，充分溶解，通入氩气保护，在三次冻融循环后，通过微量注射器注...
【技术特征摘要】
1.一种具有抗菌和促进伤口愈合功能的热诱导不可逆复合水凝胶的制备方法，其特征在于包括如下步骤：步骤1：取10～30g聚乙二醇和1～5g三乙胺溶解在二氯甲烷中，通入氩气保护后，加入2～8g2-溴代异丁酰溴，将溶液在0℃下搅拌1小时，然后在室温下再搅拌24～72小时，所得产物经铝柱分离、透析、冻干后，获得原子转移自由基聚合引发剂；步骤2：将步骤1获得的所述原子转移自由基聚合引发剂取0.1～0.5g溶解在异丙醇/水混合溶剂中，放入至聚合瓶，然后加入1～10g温敏性单体、0.1～0.5g疏水性单体、10～50mg氯化亚铜，充分溶解，通入氩气保护，在三次冻融循环后，通过微量注射器注射50～150μL三(2-二甲氨基乙基)胺开始聚合，室温下反应24～72小时，所得产物经铝柱分离、透析、冻干后，获得共聚物；步骤3：取100～300mg氧化石墨烯片加入到100～300mL蒸馏水中，超声分散后...
【专利技术属性】
技术研发人员：何涛，孙天赐，闫旭，方蔚伟，陆杨，徐晓莉，
申请(专利权)人：合肥工业大学，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。