一种分散红染料组合物及制备方法技术

技术编号:20648077 阅读:65 留言:0更新日期:2019-03-23 04:09
本发明专利技术公开了一种分散红染料组合物及制备方法。一种分散红染料组合物,按重量百分比,由以下组份组成:25.0%~35.0%的染料单体A、55.0%~65.0%的染料单体B、5.0%~15.0%的染料单体C、0.25%~0.75%染料单体D、余量为助剂。本发明专利技术可解决单一染料染色缺陷的技术问题。此染料组合物的相容性极好,提升力、上染率、得色率、均染性均比一般分散染料要好,可用于涤纶及其混纺织物的染色和印花,也可用于超细纤维的染色,染后得色量高、均染性好、各项牢度佳。

A disperse red dye composition and its preparation method

The invention discloses a disperse red dye composition and a preparation method thereof. A disperse red dye composition is composed of 25.0%~35.0% dye monomer A, 55.0%~65.0% dye monomer B, 5.0%~15.0% dye monomer C, 0.25%~0.75% dye monomer D and auxiliary agent. The invention can solve the technical problem of single dye dyeing defect. The dyestuff composition has excellent compatibility, better lifting power, dye uptake, color yield and even dyeing performance than general disperse dyes. It can be used for dyeing and printing of polyester and its blended fabrics, as well as for dyeing of ultrafine fibers. It has high color yield, good uniformity and good fastness after dyeing.

【技术实现步骤摘要】
一种分散红染料组合物及制备方法
本专利技术涉及一种分散红染料组合物,主要用于涤纶及其混纺织物的染色和印花,也可用于超细纤维的染色。
技术介绍
由于传统的分散红167#是一种应用较为广泛的染料,作为深三原之一的色系,其用量相对较大,占有一定的染料市场销售份额,但该染料单独应用时上色率、升华牢度较差,并且在纺织印染过程中对环境的污染较大,无法满足企业产品出口的需要。而且分散红167#的pH值适用范围太狭隘,且在一般涤纶纤维染色时就存在均染性差、初染速率快,纤维内相扩散慢,在染色工艺控制较松时,易造成色花、色斑、色差等一系列常见问题,用在纤度细、比表面积大的超细纤细上这些问题更加突出。国内已有类似专利,解决代替分散红167的染色问题,如中国专利ZL200510050374.5,采用分散红145#、分散红153#、分散红73#三种染料单体拼混复合,还有中国专利ZL200710069289.2,采用分散红MN、C.I.分散红50、C.I.分散紫63三种染料单体复配而成的复合型分散染料,来代替分散红167。以上染料各有优缺点。通过拼混增效,解决单一染料染色缺陷、多样化牢度和色光要求是目前染料行业本文档来自技高网...

【技术保护点】
1.一种分散红染料组合物,按重量百分比,由以下组份组成:其特征在于:25.0%~35.0%如式(1)所示的染料单体A:

【技术特征摘要】
1.一种分散红染料组合物,按重量百分比,由以下组份组成:其特征在于:25.0%~35.0%如式(1)所示的染料单体A:55.0%~65.0%如式(2)所示的染料单体B:5.0%~15.0%如式(3)所示的染料单体C:0.25%~0.75%如式(4)所示的染料单体D:余量为助剂。2.根据权利要求1中所述的一种分散红染料组合物,其特征在于:由以下组份组成:28.0%~32.0%的染料单体A,58.0%~62.0%的染料单体B,8.0%...

【专利技术属性】
技术研发人员:李万春方标朱燕英余丽娟吴勋
申请(专利权)人:杭州申航新材料有限公司
类型:发明
国别省市:浙江,33