The invention discloses a long-acting heat-resistant polypropylene composition and its preparation method. The composition comprises the following components and weight fractions: 56-85 parts of polypropylene resin, 10-20 parts of toughener, 5-20 parts of filler, 0.5-2 parts of pigments and 0.2-2 parts of antioxidant, among which the antioxidant is the product of reaction of pentaerythritol with p-hydroxybenzene fatty acids. The self-synthesized macromolecule antioxidant added in the long-term heat-resistant polypropylene composition of the invention has the characteristics of high molecular weight, no precipitation and long-term effect, and can effectively improve the heat-resistant aging grade of the polypropylene composite material.
【技术实现步骤摘要】
一种长效耐热聚丙烯组合物及其制备方法
本专利技术涉及高分子材料
,尤其涉及一种长效耐热聚丙烯组合物及其制备方法。
技术介绍
聚丙烯PP,半结晶性塑料,具有密度低、易加工等特点,已成为车用塑料中用量最大的品种。然而聚丙烯耐热老化性能差,不能满足材料在长效耐热老化的使用要求。为了提高聚丙烯的耐热老化性能,常添加抗氧剂。但是这些抗氧剂都容易析出,容易造成外观不良。这也导致了常规抗氧剂无法起到长效耐热作用。因此,本领域尚需开发一种新型耐热氧化改性聚丙烯复合材料。
技术实现思路
本专利技术的目的,就是为了解决上述问题而提供了一种长效耐热聚丙烯组合物及其制备方法,通过选用自主合成的多官能团高分子量抗氧剂,在聚丙烯材料中形成均匀分散,并且不会迁移至表面,同时增加了聚丙烯材料的长效耐热性能。本专利技术的目的是这样实现的:本专利技术的一种长效耐热聚丙烯组合物包括如下组分及重量份数:抗氧剂为季戊四醇与对羟基苯脂肪酸类物质反应产物,合成条件如下:将季戊四醇与对羟基苯脂肪酸类物质按照摩尔比1:4进行混合,在40-100℃下搅拌反应60-180min,最后将混合物在0.02MPa-0.1MPa真空度下进行真空旋蒸,温度60℃,时间0.5h,将反应产生的水除掉即可。上述的一种长效耐热聚丙烯组合物中对羟基苯脂肪酸类物质的结构如下:其中n的值范围为20~25。上述的一种长效耐热聚丙烯组合物中聚丙烯树脂为共聚聚丙烯树脂,在230℃,2.16Kg负荷下熔体质量流动速率为30~100g/10min。上述的一种长效耐热聚丙烯组合物中增韧剂包括乙烯-丁烯共聚物和/或乙烯-辛烯共聚物;优选的,增韧 ...
【技术保护点】
1.一种长效耐热聚丙烯组合物,其特征在于,包括如下组分及重量份数:
【技术特征摘要】
1.一种长效耐热聚丙烯组合物,其特征在于,包括如下组分及重量份数:所述抗氧剂为季戊四醇与对羟基苯脂肪酸类物质反应产物,合成条件如下:将季戊四醇与对羟基苯脂肪酸类物质按照摩尔比1:4进行混合,在40-100℃下搅拌反应60-180min,最后将混合物在0.02MPa-0.1MPa真空度下进行真空旋蒸,温度60℃,时间0.5h,将反应产生的水除掉即可。2.如权利要求1所述的一种长效耐热聚丙烯组合物,其特征在于,所述对羟基苯脂肪酸类物质的结构如下:其中n的值范围为20~25。3.如权利要求1所述的一种长效耐热聚丙烯组合物,其特征在于,所述聚丙烯树脂为共聚聚丙烯树脂,在230℃,2.16Kg负荷下熔体质量流动速率为30~100g/10min。4.如权利要求1所述的一种长效耐热聚丙烯组合物,其特征在于,所述增韧剂包括乙烯-丁烯...
【专利技术属性】
技术研发人员:王海霞,卢先博,陈延安,袁绍彦,黄河生,
申请(专利权)人:上海金发科技发展有限公司,江苏金发科技新材料有限公司,
类型:发明
国别省市:上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。