The invention provides a one-step preparation method of two-dimensional boron aminonide. Tripartite boron nitride was prepared by heating reaction with sodium amino and boron oxide as precursors. The powder of tripartite boron nitride was mixed with urea and then put into a ball mill tank, washed into nitrogen as protective gas, and ball milled at room temperature to obtain two-dimensional boron nitride. In the method disclosed by the invention, urea not only helps to peel off, but also protects boron nitride nanosheets from excessive mechanical damage and extensive formation of lattice defects. The two-dimensional boron nitride nanosheets arranged in ABC mode obtained by peeling off trigonal boron nitride are easier to peel off, and the dispersion performance of boron nitride in solution can be greatly improved by modifying the surface of boron nitride with amino groups. It has the characteristics of simple preparation, low cost and easy industrial mass production.
【技术实现步骤摘要】
二维氨基化氮化硼的一步制备方法
本专利技术涉及二维功能化氮化硼制备领域，尤其涉及一种由三方氮化硼一步球磨制备二维氨基化氮化硼纳米片的方法。
技术介绍
三方氮化硼化学稳定性高，在空气中的抗氧化温度接近900℃，具有很高的电阻率，发光位置在紫外光波段，可作为优良的高温耐火材料、电子器件的绝缘膜、紫外或者深紫外的发光材料等，在高温、大功率、高速半导体器件和热沉材料方面也具有很广阔的应用前景。六方氮化硼，每一层都是由B原子和N原子按照sp2杂化方式交替排列组成的无限延伸的六边形，这些原子层再沿C轴方向按照ABAB……方式排列，晶格常数a＝b＝0.25nm，c＝0.66nm，在同一层内，B和N原子之间靠共价键结合起来，层与层之间则以范德华力相结合。三方氮化硼属于三方晶系，它的结构和六方氮化硼非常相似，每一层同样是由B原子和N原子按照sp2杂化方式交替排列组成的无限延伸的六边形网格，区别是这些原子层在C轴方向上按照ABCABC……方式排列，晶格常数a＝b＝0.25nm，c＝1.00nm，在每一层内，B和N原子之间靠很强的共价键结合起来，层与层之间则以弱的范德华力相结合。剥离三...
【技术保护点】
1.二维氨基化氮化硼的一步制备方法，包括如下步骤：(1)以氨基钠和氧化硼作为反应前驱体，放入高压釜中，加热进行反应，产物用浓盐酸和去离子水清洗后，在真空烘箱里烘干备用；(2)将三方氮化硼粉末与尿素混合后放入球磨罐中，冲入氮气作为保护气，常温下球磨，得到二维氨基化氮化硼。
【技术特征摘要】
1.二维氨基化氮化硼的一步制备方法，包括如下步骤：(1)以氨基钠和氧化硼作为反应前驱体，放入高压釜中，加热进行反应，产物用浓盐酸和去离子水清洗后，在真空烘箱里烘干备用；(2)将三方氮化硼粉末与尿素混合后放入球磨罐中，冲入氮气作为保护气，常温下球磨，得到二维氨基化氮化硼。2.根据权利要求1所述的制备方法，其特征在于，步骤(1)中的氨基钠与氧化硼的摩尔数比为12∶5。3.根据权利要求1所述的制备方法，其特征在于...
【专利技术属性】
技术研发人员：苗中正，张立云，苗爱民，
申请(专利权)人：盐城师范学院，
类型：发明
国别省市：江苏,32