The invention provides a preparation method of two-dimensional boron nitride. Tripartite boron nitride was synthesized by heating reaction with sodium amino and ammonium fluoroborate as precursors and spongy nickel as catalyst. Tripartite boron nitride powder was added to dimethylformamide, dispersed by ultrasound and removed by centrifugation from large volume of boron nitride particles to obtain stripped two-dimensional boron nitride powder. The method disclosed in the invention peels two-dimensional boron nitride nanosheets arranged in ABC mode obtained by trigonal boron nitride, which is different from the traditional method peeling two-dimensional boron nitride nanosheets arranged in ABC mode obtained by hexagonal boron nitride, and the sheet layer is easier to peel off, and has the characteristics of simple preparation, low cost and easy industrial batch production.
【技术实现步骤摘要】
一种二维氮化硼的制备方法
本专利技术涉及二维氮化硼制备领域，尤其涉及一种剥离三方氮化硼制备二维氮化硼纳米片的方法。
技术介绍
石墨烯及类石墨烯二维材料的结构、性质及潜在的应用，越来越引起研究人员的广泛关注。六方氮化硼，俗称“白石墨”，具有与石墨相似的层状晶体结构，每一层都是由B原子和N原子按照sp2杂化方式交替排列组成的无限延伸的六边形，这些原子层再沿C轴方向按照ABAB……方式排列。在同一层内，B和N原子之间靠共价键结合起来，层与层之间则以范德华力相结合。二维氮化硼纳米片具有良好的润滑性、电绝缘性、耐化学腐蚀性、高热导率等，可用作润滑剂、耐火材料、抗氧化添加剂、绝缘材料、散热部件、热屏蔽材料、防止中子辐射的包装材料、耐高温电子器件材料和很有前途的声光电材料等。三方氮化硼属于三方晶系，它的结构和六方氮化硼非常相似，二者的晶体结构均类似于石墨的层状结构特征，每一层都是由B原子和N原子按照sp2杂化方式交替排列组成的无限延伸的六边形网格，区别是这些原子层在C轴方向上按照ABCABC……方式排列。在每一层内，B和N原子之间靠很强的共价键结合起来，层与层之间则以弱的范德华...
【技术保护点】
1.一种二维氮化硼的制备方法，包括如下步骤：(1)以氨基钠和氟硼酸铵作为反应前驱体，海绵状的镍做催化剂，放入高压釜，氮气为保护气，加热进行反应，产物用浓盐酸和去离子水清洗后，在真空烘箱里烘干备用；(2)将三方氮化硼粉末加入到二甲基甲酰胺中，超声分散，离心分离去除大体积的氮化硼颗粒，将上清液烘干，得到剥离好的二维氮化硼粉末。
【技术特征摘要】
1.一种二维氮化硼的制备方法，包括如下步骤：(1)以氨基钠和氟硼酸铵作为反应前驱体，海绵状的镍做催化剂，放入高压釜，氮气为保护气，加热进行反应，产物用浓盐酸和去离子水清洗后，在真空烘箱里烘干备用；(2)将三方氮化硼粉末加入到二甲基甲酰胺中，超声分散，离心分离去除大体积的氮化硼颗粒，将上清液烘干，得到剥离好的二维氮化硼粉末。2.根据权利要求1所述的制备方法，其特征在于，步骤(1)中的氨基钠、氟硼酸铵和镍的摩尔数比为0.225∶0.0283∶0...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。