一种纳米结合低气孔高纯电熔石英制品及制备方法技术

本发明专利技术公开一种高纯度、低气孔、抗侵蚀性能好、耐磨性能高、纳米结合的电熔石英制品及制备方法,本发明专利技术的原始料为：电熔石英骨料、电熔石英细粉;结合剂为纳米级液体二氧化硅,添加剂为纳米级粉体二氧化硅;电熔石英骨料40‑70份，电熔石英细粉30‑60份，纳米级液体二氧化硅0.1‑5份，纳米级粉体二氧化硅0.1‑5份;本发明专利技术还采用了低温弱氧还原快速烧成制度。

A nano-bonded low-porosity and high-purity fused quartz product and its preparation method

The invention discloses a fused quartz product with high purity, low porosity, good corrosion resistance, high wear resistance and nano-combination and a preparation method. The raw materials of the invention are: fused quartz aggregate and fused quartz fine powder; binder is nano-level liquid silica, additive is nano-level powder silica; fused quartz aggregate is 40 to 70, fused quartz fine powder is 30 to 60, nano. The invention also adopts a low temperature weak oxygen reduction rapid firing system.

【技术实现步骤摘要】
一种纳米结合低气孔高纯电熔石英制品及制备方法
本专利技术涉及一种电熔石英制品，尤其涉及一种高纯度、低气孔、抗侵蚀性能好、耐磨性能高、纳米结合的电熔石英制品及制备方法。
技术介绍
目前,焦炉是炼焦的主要热工设备。焦炉炉体由炉顶、燃烧室和炭化室、斜道区、蓄热室等部分，并通过烟道和烟囱相连,主要部位由硅砖砌成，为使密封性好，要采用异形砖进行砌筑。然而，焦炉硅砖在使用过程中承受煤在炭化期间膨胀产生的压力，以及装煤、推焦和出焦引起的磨损和剥落。磨损和剥落会导致耐火砖表面粗糙，而这会导致焦炉炭化室状态变差，推焦负荷增大。另外,在玻璃窑的碹部、加料口等部位的硅砖长期在高温下受碱蒸汽以及混合飞料的侵蚀，加上高温荷重的影响，长期使用会发生砖块熔化、裂纹掉块等现象,而这些现象会污染玻璃液，影响产出成品的质量。本专利技术解决了上述问题。
技术实现思路
本专利技术的目的是克服现有硅砖抗碱侵蚀性差、易磨损剥落的问题，提出一种高纯度、低气孔、抗侵蚀性能好、耐磨性能高、纳米结合的电熔石英制品及制备方法。为了实现上述目的，本专利技术采用的技术方案为：本专利技术所述的纳米结合低气孔高纯电熔石英制品，原始料为：电熔石英骨料本文档来自技高网...

【技术保护点】
1.一种纳米结合低气孔高纯电熔石英制品，其特征在于：原始料为：电熔石英骨料、电熔石英细粉; 结合剂为纳米级液体二氧化硅, 添加剂为纳米级粉体二氧化硅, 加入重量份数为：电熔石英骨料40‑70份，电熔石英细粉30‑60份，纳米级液体二氧化硅0.1‑5份，纳米级粉体二氧化硅0.1‑5份。

【技术特征摘要】
1.一种纳米结合低气孔高纯电熔石英制品，其特征在于：原始料为：电熔石英骨料、电熔石英细粉;结合剂为纳米级液体二氧化硅,添加剂为纳米级粉体二氧化硅,加入重量份数为：电熔石英骨料40-70份，电熔石英细粉30-60份，纳米级液体二氧化硅0.1-5份，纳米级粉体二氧化硅0.1-5份。2.根据权利要求1所述的一种纳米结合低气孔高纯电熔石英制品，其特征在于：电熔石英骨料，纯度＞99.99%，粒度≤5mm。3.根据权利要求2所述的一种纳米结合低气孔高纯电熔石英制品，其特征在于：电熔石英骨料的形状为球形。4.根据权利要求1所述的一种纳米结合低气孔高纯电熔石英制品，其特征在于：电熔石英细粉，纯度＞99.99%，粒度≤0.09mm。5.根据...