The invention discloses a production method of special fused quartz sand for packaging, which belongs to the field of quartz fine processing; the invention takes fused quartz blocks with grain size of 10-20 mm as raw materials, and takes crusher, vibrating screen and magnetic separator as equipment to produce fused quartz sand for packaging by crushing, grading and magnetic separation of fused quartz blocks; the production method has the following advantages: less investment in equipment; It can produce high quality fused quartz sand for packaging. The product is a special material for packaging in semiconductor integrated circuit industry.
【技术实现步骤摘要】
一种封装专用熔融石英砂的生产方法
本专利技术属于石英精加工领域，尤其涉及一种封装专用熔融石英砂的生产方法。
技术介绍
熔融石英是二氧化硅的非晶态，其二氧化硅的含量不得少于99.8%，生产时将精选的优质石英砂在电弧炉、电阻炉或高温烧结炉内熔融，熔融温度为1800℃-1900℃熔融约12小时后成为熔融状态，冷却后成为熔融石英，由于其原子结构长程无序，其三维结构交叉链接可使熔融石英具有使用温度高、热膨胀系数低，常温下不与其它物质反应，耐磨性能好，硬度较高、耐高温性能强，透光折射性能、压电性能优异。封装用熔融石英砂的规格为1.5—3.0毫米，外观为白色或半透明状结晶状，其特点是SiO2含量在99.99%以上；生产该产品以粒度10—20毫米的熔融石英块为原料，通过破碎、筛分、磁选等一系列工艺加工而成，该工艺的主要优点是：所用设备少、投资小、无有毒有害气体和液体排放、产品质量好、可批量生产并生产出高质量的封装专用熔融石英砂。
技术实现思路
本专利技术主要解决的问题是提供一种封装专用熔融石英砂的生产方法，该方法以粒度10—20毫米的熔融石英块为原料，以破碎机、振动筛、磁选机为设备来...
【技术保护点】
1.一种封装专用熔融石英砂的生产方法，该方法以粒度10—20毫米的熔融石英块为原料，以破碎机、振动筛、磁选机为设备来生产封装用熔融石英砂；其特征是：（1）将规格为10—20毫米熔融石英块送入破碎机进行破碎，破碎时间为0.3‑0.4小时，破碎后的所有颗粒送入进行筛分振动筛，去除大于3毫米和小于1.5毫米的石英砂，得到1.5‑3.0毫米的石英砂；（2）将1.5‑3.0毫米的石英砂送入磁选机，利用磁选机内的磁场将含磁、含金属的石英砂进行分离去除，磁选时间为0.35‑0.40小时，得到高纯石英砂封装用熔融石英砂。
【技术特征摘要】
1.一种封装专用熔融石英砂的生产方法，该方法以粒度10—20毫米的熔融石英块为原料，以破碎机、振动筛、磁选机为设备来生产封装用熔融石英砂；其特征是：（1）将规格为10—20毫米熔融石英块送入破碎机进行破碎，破碎时间为0.3-0.4小时，破碎后的所有颗粒送入进行筛分振动筛，去除大于3毫米和小于1.5毫米的石英砂，得到1.5-3.0毫米的石...
【专利技术属性】
技术研发人员：郭涛，
申请(专利权)人：江苏锡沂高新区科技发展有限公司，
类型：发明
国别省市：江苏,32