A method for recovering and utilizing a negatives includes: crushing the negatives, the negatives include a polyester resin base and a photosensitive emulsion formed on the base, the photosensitive emulsion contains silver particles; immersing the broken negatives in an alkali solution at a temperature of 10 60, so that the alkali solution dissolves the photosensitive emulsion of the negatives, thereby enabling the negatives to be dissolved. The silver particles in the photosensitive emulsion fall off from the negative; the negative is removed from the alkali solution and cleaned to obtain a polyester resin matrix; and the alkali solution is filtered to obtain silver particles.
【技术实现步骤摘要】
底片的回收利用方法
本专利技术涉及一种废液回收利用领域，尤其涉及一种底片的回收利用方法。
技术介绍
在印刷电路板制造领域，通常需要将符合规格的线路感光至底片，经冲片后制得负片，在后续曝光显影过程中，负片上的线路图案将转移至电路基板上。黑白底片的片基的主要成份是聚酯树脂(如PET)，片基上涂布有单层或多层感光乳剂。该感光乳剂的成份为明胶(Gelatin)以及悬浮在明胶中的卤化银(Silverhalide)。在冲片过程中，部分卤化银感光而转变为黑色的金属银颗粒，经显影、定影工艺后固定于片基，而未感光的卤化银则在定影时溶解于定影液。此类底片对环境有污染，通常需要对负片进行处理后才能将其丢弃，避免对环境造成污染，而底片的处理工艺(如焚烧法、硝酸浸泡法)会产生大量的有害产物。
技术实现思路
有鉴于此，有必要提供一种底片的回收利用方法，能够解决以上问题。本专利技术提供一种底片的回收利用方法，包括：将所述底片进行破碎处理，所述底片包括聚酯树脂片基以及形成于所述片基上的感光乳剂，所述感光乳剂中含有银颗粒；将破碎后的所述底片浸没于温度为10℃-60℃的一碱溶液中，使所述碱溶液溶解所述底...
【技术保护点】
1.一种底片的回收利用方法，包括：将所述底片进行破碎处理，所述底片包括聚酯树脂片基以及形成于所述片基上的感光乳剂，所述感光乳剂中含有银颗粒；将破碎后的所述底片浸没于温度为10℃‑60℃的一碱溶液中，使所述碱溶液溶解所述底片的感光乳剂，从而使所述感光乳剂中的银颗粒从所述底片上脱落；将所述底片从所述碱溶液中取出并清洗，从而得到聚酯树脂片基；以及过滤所述碱溶液，从而得到银颗粒。
【技术特征摘要】
1.一种底片的回收利用方法，包括：将所述底片进行破碎处理，所述底片包括聚酯树脂片基以及形成于所述片基上的感光乳剂，所述感光乳剂中含有银颗粒；将破碎后的所述底片浸没于温度为10℃-60℃的一碱溶液中，使所述碱溶液溶解所述底片的感光乳剂，从而使所述感光乳剂中的银颗粒从所述底片上脱落；将所述底片从所述碱溶液中取出并清洗，从而得到聚酯树脂片基；以及过滤所述碱溶液，从而得到银颗粒。2.如权利要求1所述的底片的回收利用方法，其特征在于，使用具有双轴式刀具的碎纸机对所述底片进行破碎处理。3.如权利要求1所述的底片的回收利用方法，其特征在于，所述聚酯树脂片基的材质为聚对苯二甲酸乙二醇酯。4.如权利要求...
【专利技术属性】