The invention discloses a cleaning method for silver-based solder, which comprises the following specific steps: (1) putting silver-based solder into alkaline solution for ultrasonic vibration 180-300 s; (2) putting silver-based solder into pure water for washing, ultrasonic vibration 60-120 s; liquid temperature 70-80 degrees; (3) repeating steps (1) - (2) recycling 1-2 times; (4) putting silver-based solder into cleaning solution. Ultrasound vibration is 60-100s; (5) Silver-based solder is taken out and vibrated 120-180s with pure water; (6) Silver-based solder is taken out and immersed in 99.9% alcohol for 30-40s, then dried. The invention has the advantages of simple operation, low cost, good cleaning effect and environmental protection, and can be used in industrial production.
【技术实现步骤摘要】
一种银基焊料的清洗方法
本专利技术涉及焊料
，尤其是涉及一种对银基焊料的清洗方法。
技术介绍
银基焊料主要是银铜基二元或多元合金材料，具有优异的加工性能，润湿性能及流淌性能良好，强度、塑性、导电、耐蚀等性能优异，可作为金属与金属、金属与陶瓷焊接最佳连接材料，因而得到广泛的应用。在银基焊料合金的多次轧制过程中会使用不同溶度轧制油，因此轧制完成的银基焊料合金带材表面上会附着轧制油污；并且合金带材在运输的过程中，遇到高温、高湿环境容易被氧化和腐蚀。真空电子封接气密性要求较高，封接用焊料表面的油污和氧化皮会导致焊缝无法达到气密性要求。在实际使用中，通过对焊料清洗以满足使用要求。通常的方法是水洗法和电解法。但是水洗法清洗不彻底，电解法成本太高，因此开发一种方便简单的清洗方法迫在眉睫。
技术实现思路
针对现有技术存在的上述问题，本申请人提供了一种银基焊料的清洗方法。本专利技术方法操作简单，成本低，清洗效果好，环保，可以用于工业化生产中。本专利技术的技术方案如下：一种银基焊料的清洗方法，所述方法包括如下具体步骤：(1)将银基焊料放入碱性溶液中超声波振动180～300s；(2)...
【技术保护点】
1.一种银基焊料的清洗方法，其特征在于，所述方法包括如下具体步骤：(1)将银基焊料放入碱性溶液中超声波振动180～300s；(2)将银基焊料放入纯水中进行漂洗，超声波振动60～120s；液体温度为70～80℃；(3)将步骤(1)～(2)重复循环1～2次；(4)然后银基焊料放入清洗剂溶液中，超声波振动60～100s；(5)将银基焊料取出用纯水超声波振动120～180s；(6)将银基焊料取出在浓度为99.9％酒精中浸泡30～40s，然后烘干即可。
【技术特征摘要】
1.一种银基焊料的清洗方法，其特征在于，所述方法包括如下具体步骤：(1)将银基焊料放入碱性溶液中超声波振动180～300s；(2)将银基焊料放入纯水中进行漂洗，超声波振动60～120s；液体温度为70～80℃；(3)将步骤(1)～(2)重复循环1～2次；(4)然后银基焊料放入清洗剂溶液中，超声波振动60～100s；(5)将银基焊料取出用纯水超声波振动120～180s；(6)将银基焊料取出在浓度为99.9％酒精中浸泡30～40s，然后烘干即可。2.根据权利要求1所述的银基钎料的清洗方法，其特征在于，所述碱性溶液为肥皂溶液或洗衣粉溶液；所属碱性溶液的质量浓度为15～25％。3.根据权利要求1所述的银基钎料的清洗方法，其特...
【专利技术属性】
技术研发人员：晏弘，
申请(专利权)人：无锡日月合金材料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。