本发明专利技术涉及涂料固化技术领域，尤其是一种粉末涂料固化方法，经过将步骤(2)中在常温下采用近红外范围射线照射2s中，实现预热，并结合UV辐射已经预热的粉末涂料，并增加热量，使得熔融流平之后，再在UV辐射下进行辐照固化，并控制熔融前后的UV辐射剂量，使得固化成型的涂层光泽度(60°)稳定在95‑105％之间，降低了幅度，降低了特定涂层制备难度。

A Curing Method of Powder Coatings

The invention relates to the field of coating curing technology, in particular to a powder coating curing method, which realizes preheating by irradiating near infrared radiation for 2 seconds at room temperature in step (2) and combining with the powder coatings that have been preheated by UV radiation, and increasing heat so that after melting and leveling, the powder coatings are cured by irradiation under UV radiation, and the UV radiation dose before and after melting is controlled to make the powder coatings cured. The glossiness (60 degrees) of the cured coatings is stable between 95 105%, which reduces the extent and the difficulty of the preparation of specific coatings.

【技术实现步骤摘要】
一种粉末涂料固化方法
本专利技术涉及涂料固化
，尤其是一种粉末涂料固化方法。
技术介绍
在金属的涂层中，采用粉末涂料喷涂形成的装饰或功能性表面涂层，获得了广泛的应用。该方法效率高，并且具有较优的环保性能；同时，粉末涂料也得到了大量了开发和研究，使得能够满足各种需求的粉末涂料均具有，降低了喷涂处理的原料成本。目前，粉末涂料固化方法是：先通过加热到超过粉末涂料玻璃化转变温度或者熔点温度，使得喷涂到基材表面的粉末熔融，再实现的降温固化过程，例如对流炉、红外辐射器或者将二者的结合作为热源，实现热固化处理；而在这一过程中，通常需要使得粉末涂料处于140-200℃下加热10-30min左右，才能够实现上述功效。鉴于此，有研究者就粉末涂料喷涂在基材表面后的固化方法做出了研究，例如专利号为ZL99813212.8的粉末喷漆的固化方法，采用近红外范围射线(NIR射线)辐射，使得粉末喷漆固化，实现在特定时间内，借助辐射达到粉末喷涂基材的表面温度，经过控制硫酸钡和/或氧化铝、炭黑等的含量，实现的固化过程，使得与现有的固化方法相比，在相同的辐射条件下，能够达到5s的固化时间。再如专利号为2005800本文档来自技高网...

【技术保护点】
1.一种粉末涂料固化方法，其特征在于，包括以下步骤：(1)将粉末涂料采用喷枪机喷涂在基材表面；(2)在常温环境下，采用强度分布介于波长范围800‑900nm的近红外范围射线照射2s后，采用UV辐射辐照粉末涂料，经过增加温度使得粉末涂料熔融、流平，形成熔融涂层，UV辐射辐照下固化；其中，在熔融前，采用的UV辐射辐照剂量为200‑230mJ/cm2；在熔融之后，将UV辐射辐照剂量调整为35‑45mJ/cm2。

【技术特征摘要】
1.一种粉末涂料固化方法，其特征在于，包括以下步骤：(1)将粉末涂料采用喷枪机喷涂在基材表面；(2)在常温环境下，采用强度分布介于波长范围800-900nm的近红外范围射线照射2s后，采用UV辐射辐照粉末涂料，经过增加温度使得粉末涂料熔融、流平，形成熔融涂层，UV辐射辐照下固化；其中，在熔融前，采用的UV辐射辐照剂量为200-230mJ/cm2；在熔融之后，将UV辐射辐照剂量调整为35-45mJ/cm2。2.如权利要求1所述的粉末涂料固化方法，其特征在于，所述的在熔融前，采用的UV辐射辐照剂量为210-220...

【专利技术属性】
技术研发人员：周光勇，许仁贵，刘元长，陈应先，胡强，
申请(专利权)人：遵义春华新材料科技有限公司，
类型：发明
国别省市：贵州,52