本发明专利技术公开了一种硬质合金材料，包括以下按重量百分比计的原料：WC粉91.5～92.5％，Co粉5～6％，Cu粉0.5～0.8％，Fe粉0.5～1％，Ti粉0.3～0.5％，TiB2粉0.3～0.5％。还公开了其制备方法。本发明专利技术以WC为硬质相，Co、Cu、Fe、Ti为粘结相，TiB2为增强相，上述组分搭配能显著提高WC基质的硬度和耐磨性，实验表明，本发明专利技术具有较高的常温硬度和高温硬度，有利于改善WC‑Co硬质合金的高温耐磨性。

A Cemented Carbide Material and Its Preparation Method

The invention discloses a cemented carbide material, which comprises the following raw materials by weight percentage: WC powder 91.5-92.5%, Co powder 5-6%, Cu powder 0.5-0.8%, Fe powder 0.5-1%, Ti powder 0.3-0.5%, TiB2 powder 0.3-0.5%. The preparation method is also disclosed. The present invention takes WC as hard phase, Co, Cu, Fe, Ti as bonding phase, TiB2 as reinforcing phase. The hardness and wear resistance of WC matrix can be significantly improved by the combination of the above components. Experiments show that the present invention has higher room temperature hardness and high temperature hardness, and is beneficial to improving the high temperature wear resistance of WC Co Co cemented carbide.

【技术实现步骤摘要】
一种硬质合金材料及其制备方法
本专利技术涉及硬质合金材料
，具体涉及一种以WC为基体的硬质合金材料及其制备方法。
技术介绍
硬质合金通常指以钛、铪、钒、铌、铬、钨等过渡金属碳化物为硬质相，以铁族元素(铁、钴、镍)粉末为粘结相采用粉末冶金技术烧结而成材料，具有模量高、强度大、热膨胀系数低及化学性质稳定等优点，广泛应用于精密制造、磨具及对耐蚀性和耐磨性要求较高的领域。其中，WC-Co硬质合金由于具有高强度、高硬度等优点，被广泛用于钻进、采矿、切削等对耐磨性要求较高的领域。但是，在高温烧结时，WC晶粒可能异常长大，影响合金的力学性能及耐高温性能，特别是当温度高于600℃时，易造成合金硬度急剧下降，限制了材料的应用范围。比如在切削过程中，工件与道具的机械摩擦可能会释放大量的热能，若刀刃硬度降低，极易损伤工件表面，影响切削质量及刀具的使用寿命。
技术实现思路
针对现有技术存在的上述不足，本专利技术的目的提供一种高温耐磨性优异的WC-Co硬质合金材料及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种硬质合金材料，包括以下按重量百分比计的原料：WC粉91.5～92.5％，Co粉5～6本文档来自技高网...

【技术保护点】
1.一种硬质合金材料，其特征在于，包括以下按重量百分比计的原料：WC粉91.5～92.5％，Co粉5～6％，Cu粉0.5～0.8％，Fe粉0.5～1％，Ti粉0.3～0.5％，TiB2粉0.3～0.5％。

【技术特征摘要】
1.一种硬质合金材料，其特征在于，包括以下按重量百分比计的原料：WC粉91.5～92.5％，Co粉5～6％，Cu粉0.5～0.8％，Fe粉0.5～1％，Ti粉0.3～0.5％，TiB2粉0.3～0.5％。2.根据权利要求1所述的硬质合金材料，其特征在于，所述WC粉、Co粉、Cu粉、Fe粉、Ti粉和TiB2粉的粒径独立为1～10μm。3.一种硬质合金材料的制备方法，其特征在于，包括步骤：S1、将权利要求1或2所述的原料混匀，加入球磨机中，加入石蜡进行湿磨，然后真空干燥，过100～200目筛，得到混合均匀的合金粉末；S2、将步骤S...