The invention discloses a method for solving the cold bending crack at the root of the transverse rib of threaded steel. The transverse rib chamfering method is adopted: after the roll groove is milling the transverse rib with the normal thread milling cutter, the chamfering milling cutter head is replaced, and after the tool is re-aligned, the depth of the chamfering milling cutter is about 0.7 mm at the base width of the transverse rib, so as to increase the base width of the transverse rib and the contact area The invention has the advantages of increasing the bottom width of the transverse rib, increasing the contact area between the bottom of the transverse rib and the base circle, reducing the stress state and concentration phenomenon at the root of the transverse rib during cold bending of the threaded steel, and improving the cold bending crack at the root of the transverse rib.
【技术实现步骤摘要】
一种解决螺纹钢横肋根部冷弯裂纹的方法
本专利技术涉及一种钢铁行业轧钢生产线螺纹铣横肋加工方法,具体地说是一种解决螺纹钢横肋根部冷弯裂纹的方法,属于螺纹铣横肋加工方法领域。
技术介绍
现在目前国内钢厂为降低生产成本,大多采用控轧控冷工艺生产螺纹钢,但由于控冷温度较低,容易在螺纹钢做冷弯试验时横肋根部裂纹。
技术实现思路
为了解决上述问题,本专利技术设计了一种解决螺纹钢横肋根部冷弯裂纹的方法,采用倒角铣刀后,增大了横肋底宽,横肋底部与基圆增加接触面积,减少螺纹钢冷弯时横肋根部受力状态和应力集中现象,改善横肋根部冷弯裂纹。本专利技术的技术方案为:一种解决螺纹钢横肋根部冷弯裂纹的方法,采用横肋倒角方法:将轧辊轧槽利用正常螺纹铣刀铣完横肋后,更换倒角铣刀头,重新对刀后,在横肋底宽位置利用倒角铣刀吃刀深度0.7mm左右,达到增大横肋底宽、增加横肋底宽与基圆的接触面积的目的。其中,所述正常螺纹铣刀的刀头夹角为90°角;所述倒角铣刀头的夹角为135°角。正常螺纹铣刀本专利技术的优点在于:采用倒角铣刀后,增大了横肋底宽,横肋底部与基圆增加接触面积,减少螺纹钢冷弯时横肋根部受力状态和应力集中现象,改善横肋根部冷弯裂纹。下面结合附图和实施例对本专利技术作进一步说明。附图说明图1为正常螺纹铣刀刀头结构示意图;其中,左图为正常螺纹铣刀刀头的正视图,右图为正常螺纹铣刀刀头的侧视图;图2为倒角铣刀头结构示意图;其中,左图为本专利技术倒角铣刀头的正视图,右图为本专利技术倒角铣刀头的侧视图。具体实施方式以下对本专利技术的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本专利 ...
【技术保护点】
1.一种解决螺纹钢横肋根部冷弯裂纹的方法,其特征在于,采用横肋倒角方法:将轧辊轧槽利用正常螺纹铣刀铣完横肋后,更换倒角铣刀头,重新对刀后,在横肋底宽位置利用倒角铣刀吃刀深度0.7mm左右,达到增大横肋底宽、增加横肋底宽与基圆的接触面积的目的。
【技术特征摘要】
1.一种解决螺纹钢横肋根部冷弯裂纹的方法,其特征在于,采用横肋倒角方法:将轧辊轧槽利用正常螺纹铣刀铣完横肋后,更换倒角铣刀头,重新对刀后,在横肋底宽位置利用倒角铣刀吃刀深度0.7mm左右,达到增...
【专利技术属性】
技术研发人员:邵际平,王利,徐玉强,马加波,沈小二,王永强,高磊,李长江,张海燕,
申请(专利权)人:新疆昆玉钢铁有限公司,
类型:发明
国别省市:新疆,65