The invention discloses a preparation method of P-zeolite molecular sieve, which includes the following steps: calcination of A and fly ash: calcination of fly ash at 500-800 C for 2-6 hours to obtain calcined fly ash; preparation of B and P-zeolite molecular sieve: preparation of material according to the ratio of calcined fly ash: NaOH aqueous solution = 8-25g:100mL, and then mixing calcined fly ash with NaOH aqueous solution, and raising. P zeolite molecular sieves were obtained by filtering and drying the solid products obtained in the solution. In the preparation method of the invention, the fly ash raw material does not need to be co-calcined with alkali; the purity of the prepared P-type molecular sieve is high, and there are no other impurity products; the preparation process is simple, and the reaction temperature and stirring speed need not be changed in the reaction process.
【技术实现步骤摘要】
一种P型沸石分子筛的制备方法
本专利技术涉及一种P型沸石分子筛的制备方法，属于分子筛合成领域。
技术介绍
分子筛是一类具有立方晶格的硅铝酸盐化合物，主要由硅、铝通过氧桥连接组成空旷的骨架结构，在结构中有很多孔径均匀的孔道和排列整齐、内表面积很大的空穴。此外还含有电价较低而离子半径较大的金属离子和化合态的水。由于加热后水分子不断逸出，但晶体骨架结构不变，因而形成了许多大小相同的空腔，空腔又有许多直径相同的微孔相连，比孔道直径小的物质分子吸附在空腔内部，而把比孔道大得分子排斥在外，从而使不同大小形状的分子分开，起到筛分分子的作用，因而称作分子筛。沸石的种类很多，根据其来源不同，分为天然沸石和人工沸石两大类。在对天然沸石进行系统研究之后，为得到纯净的沸石，人们开始致力于人工合成沸石。到1954年，沸石的人工合成就已经工业化了。1948年，Barrer在高温高压下首次合成了小孔径的沸石，开创了沸石合成的新纪元。随着世界环保意识的增强，三聚磷酸钠作为洗涤助剂的问题得到人们的重视。P型沸石为主要洗涤用沸石，以其优良的性能和突出的特点在洗涤剂助剂中脱颖而出，成为三聚磷酸钠的最佳...
【技术保护点】
1.一种P型沸石分子筛的制备方法，其特征在于：包括有以下步骤：A、粉煤灰的煅烧：将粉煤灰在500～800℃温度下煅烧2～6小时，得到煅烧粉煤灰；B、P型沸石分子筛的制备：按照煅烧粉煤灰：NaOH水溶液＝8～25g:100mL的比例备料，然后将煅烧粉煤灰与NaOH水溶液混合，升温至60～100℃，搅拌作用下反应8～36小时；将溶液中所得固体产物过滤、干燥后，获得P型沸石分子筛。
【技术特征摘要】
1.一种P型沸石分子筛的制备方法，其特征在于：包括有以下步骤：A、粉煤灰的煅烧：将粉煤灰在500～800℃温度下煅烧2～6小时，得到煅烧粉煤灰；B、P型沸石分子筛的制备：按照煅烧粉煤灰：NaOH水溶液＝8～25g:100mL的比例备料，然后将煅烧粉煤灰与NaOH水溶液混合，升温至60～100℃，搅拌作用下反应8～36小时；将溶液中所得固体产物过滤、干燥后，获...
【专利技术属性】
技术研发人员：孙奇，王鹏，刘其斌，陈光杰，王刚，曹骏，
申请(专利权)人：贵州大学，
类型：发明
国别省市：贵州,52