The invention belongs to the technical field of semiconductor material preparation, in particular to a heterojunction material, a preparation method and a use thereof. Bismuth germanate was added to PVP solution at room temperature to obtain suspension; then CdS powder was stirred in ethanol vigorously, then CdS solution was slowly added to the suspension. After stirring, the suspension was transferred to the reactor at 160 C for hydrothermal reaction for 6 hours. The reactor was cooled to room temperature, and the visible light-responsive CdS/Bi12GeO2 0 heterojunction material was obtained by washing and drying with water and ethanol. The CdS/Bi12GeO2 0 heterojunction material is used as a photocatalytic material for photocatalytic degradation of antibiotics under visible light.
【技术实现步骤摘要】
一种异质结材料及制备方法和用途
本专利技术属于半导体材料制备
，特指一种异质结材料及制备方法和用途。利用水热法合成硫化镉(CdS)与锗酸铋(Bi12GeO20)复合成异质结材料，可用于可见光下降解抗生素。技术背景近年来，随着经济的不断发展，全球范围内的能源、环境问题也越来越严重。尤其抗生素在医药个人护理品和畜牧业方面的大规模应用，使水体环境中抗生素的污染已成为当前研究的热点问题。目前光催化技术是一种新兴的污染治理技术，具有效率高、反应条件温和等优点。早在1972年，日本学者Fujishima和Honda对光照TiO2电极导致水分解产生氢气的发现，使半导体光催化技术在氢能开发和环境治理等方面的应用基础研究迅速开展起来。但在太阳光谱中,紫外光仅占5％，而可见光的比例却高达43％，因此，为了克服传统TiO2光催化剂仅能响应紫外光的缺点，开发出可实际应用的可见光响应的半导体光催化剂是当前光催化研究领域的热点问题。由于Bi3+金属离子在许多代表性的半导体光催化剂中具有与Ga3+和Sn4+相同的电子排列，因此可用作光催化剂的可行中心金属离子。铋基氧化物被广泛认为是光...
【技术保护点】
1.一种异质结材料的制备方法，所述异质结材料为可见光响应CdS/Bi12GeO20异质结材料，其特征在于，所述制备方法的具体步骤为：将Bi12GeO20在室温下加入到PVP溶液中得到悬浮液；随后，将CdS粉末在乙醇中剧烈搅拌后，再将得到的CdS溶液缓慢加入到悬浮液中，搅拌后将悬浮液转移至反应釜中160℃水热反应6h，待反应釜冷却至室温，用水和乙醇洗样、烘干得到可见光响应CdS/Bi12GeO20异质结材料。
【技术特征摘要】
1.一种异质结材料的制备方法，所述异质结材料为可见光响应CdS/Bi12GeO20异质结材料，其特征在于，所述制备方法的具体步骤为：将Bi12GeO20在室温下加入到PVP溶液中得到悬浮液；随后，将CdS粉末在乙醇中剧烈搅拌后，再将得到的CdS溶液缓慢加入到悬浮液中，搅拌后将悬浮液转移至反应釜中160℃水热反应6h，待反应釜冷却至室温，用水和乙醇洗样、烘干得到可见光响应CdS/Bi12GeO20异质结材料。2.如权利要求1所述的一种异质结材料的制备方法，其特征在于，所述CdS与Bi12GeO20的质量比...
【专利技术属性】
技术研发人员：刘春波，阮晓文，胡灏，车慧楠，董红军，李春梅，
申请(专利权)人：江苏大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。