The invention discloses a sample for testing shell strength and its manufacturing method and strength testing method. The shell material for testing shell strength is coated by a cylindrical wax module composed of a cylindrical wax module. The structure of the sample for testing shell strength is hollow cylindrical, and the layers and wall thickness of the sample are made according to the actual number of layers and wall thickness of the casting shell. Thickness is not limited, because the current shell strength testing specimens are strip-shaped fixed size, suitable for the performance testing of shell-making materials with the same number of layers and different sizes.
【技术实现步骤摘要】
一种检测型壳强度用试样及其制造方法及其强度检测方法
本专利技术属于熔模精密铸造型壳制造领域，涉及熔模铸造型壳性能检测试样及其熔模铸造型壳性能制造，特别涉及一种检测型壳强度用试样及其制造方法及其强度检测方法。
技术介绍
在熔模铸造行业中，型壳是非常重要的一个中间过程，其性能直接影响铸件质量状况。尤其是型壳室温及高温强度，室温强度不足会引发搬运破裂；高温强度不足会发生浇注过程漏钢，轻则使得型壳及铸件报废，重则导致漏出的钢液破坏浇注设备。型壳强度过高又会导致浇注后铸件应力过大变形，型壳残余强度过高则导致型壳难以清除。综上所述，型壳强度是衡量判断型壳性能非常重要的一项指标。在现有技术中，检测型壳强度所用试样为长方形平板，其厚度为固定值，这样的板状型壳试样更适宜用来评价制壳材料。而对于评价型壳制造的工艺性，尤其是不同的型壳层数、厚度与强度之间的关系没有更直观便捷的方法，不能更好地为铸件型壳的制壳工艺改进提供更可靠的数据。
技术实现思路
本专利技术所要解决的技术问题是提供一种能更好地评价铸件型壳制造工艺的检测型壳强度用试样及其制造方法及其强度检测方法，为铸件型壳的制壳工艺的改进提...
【技术保护点】
1.一种检测型壳强度用试样，其特征在于：试样的结构为空心圆柱状。
【技术特征摘要】
1.一种检测型壳强度用试样，其特征在于：试样的结构为空心圆柱状。2.根据权利要求1所述的一种检测型壳强度用试样，其特征在于：所述试样的层数和壁厚与实际铸件型壳的层数和壁厚相同。3.根据权利要求1所述的一种检测型壳强度用试样的制造方法，其特征在于，包括以下步骤：步骤11)加工用于制作检测型壳强度用试样的蜡模，蜡模为圆柱状，并将蜡模组合成蜡模模组；步骤12)按铸件型壳制壳生产工艺或检测要求对蜡模模组涂制制壳材料，最后一层只粘涂料不敷砂；步骤13)对检测型壳强度用试样制壳后进行脱蜡，脱蜡后放置，先保温后烘干，再进行焙烧，然后保温，最后等温度下降后空冷出炉。4.根据权利要求3所述的制造方法，其特征在于：步骤11)中所述的蜡模为实心圆柱蜡模，采用蜡模模具及压蜡机制作实心圆柱蜡模。5.根据权利要求3所述的制造方法，其特征在于：步骤12)中涂制检测型壳强度用试样的制壳材料时，根据已有的制壳方法涂制检测型壳强度用试样；检测型壳强度用试样的层数和厚度按照铸件大小及工艺所需自行设计制作。6.根据权利要求3所述的制造方法，其特征在于：步骤13)中脱蜡后放置24h，先经110℃保温2h～3h后烘干，再进行焙烧，焙烧温度至850℃～1200℃，然后保温1h～2h，最后等温度降至300℃以下空冷出炉。7....
【专利技术属性】
技术研发人员：董茵，段继东，海潮，陈杰，段朋国，郭涛，潘锐，商辉，
申请(专利权)人：中国航发动力股份有限公司，
类型：发明
国别省市：陕西,61