The invention relates to a high temperature and wear resistant MCrAlSiC composite coating, which comprises high temperature oxidation resistant particles, wear resistant particles and M-base encapsulated particles. The high temperature oxidation resistant particles in the composite coating are CrAl alloy particles or mixed with Al particles using Cr particles; the hard particles are SiC, and the M base of the coated particles is Ni, Co, Fe or their combination. The preparation process is two-step electrophoresis and electrodeposition. Specifically, the dense MCrAlSiC composite coatings are obtained by electrophoretic deposition of CrAl and SiC particles to obtain porous CrAlSiC coatings with uniform distribution of particles, and then by electrodeposition of M to make it grow from CrAlSiC/matrix interface to CrAlSiC coating surface. MCrAl coating has excellent mechanical properties and high temperature oxidation resistance.
【技术实现步骤摘要】
一种耐高温耐磨MCrAlSiC复合涂层
本专利技术涉高温防护领域，具体的说是耐高温耐磨MCrAlSiC复合涂层。
技术介绍
MCrAl(Y)（M=Ni，Co，Fe或其组合）在高温下可热生长Al2O3或Cr2O3膜，进而提高热端部件的抗高温氧化和热腐蚀性能,故常用于航空发动机压气机叶片、涡轮叶片以及燃气轮机叶片。而在实际的服役过程中，摩擦磨损失效也是导致在高温下服役的结构零部件如航空发动机叶片失效的重要原因。因此，这些高温部件表面的包覆涂层不仅需要优异的抗高温氧化性能，同时也需要良好耐磨性能。现有的涂层，一般是只具有良好的抗高温氧化及热腐蚀性能，因为没有硬质颗粒而不具备较好的耐磨性能，如公开号为“CN106756819A”，名称为“一种MCrAlY高温防护涂层制备方法”的专利；或只具有优异的耐磨性能，却不含抗高温氧化元素，如公开号为CN105506526A，名称为“铝合金表面Ni-SiC复合镀层的制备方法及其电镀液”的专利，Ni-SiC复合镀层因含有SiC颗粒，故而具有较好的硬度和耐磨性能，相关专利并未研究其抗氧化性能。根据高温氧化知识，涂层在氧化环境下能热生长连续...
【技术保护点】
1.一种耐高温耐磨MCrAlSiC复合涂层，其特征是：包括抗高温氧化颗粒（1），硬质耐磨颗粒（2），包裹颗粒的基体M（3）。
【技术特征摘要】
1.一种耐高温耐磨MCrAlSiC复合涂层，其特征是：包括抗高温氧化颗粒（1），硬质耐磨颗粒（2），包裹颗粒的基体M（3）。2.根据权利要求1所述的一种耐高温耐磨MCrAlSiC复合涂层，其特征是，抗高温氧化颗粒为CrAl合金颗粒或Cr颗粒和Al颗粒混合。3.根据权利要求1所述的一种耐高温耐磨MCrAlSiC复合涂层，其特征是，包覆涂层MCrAl涂层内同时含有硬质耐磨颗粒SiC。4.根据权利要求1所述的一种耐高温耐磨MCrAl...
【专利技术属性】
技术研发人员：赵明雨，杨秀英，甄会娟，
申请(专利权)人：沈阳工学院，
类型：发明
国别省市：辽宁,21
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。