The present invention provides a carbon-coated vanadium nitride electrocatalyst, which uses carbon-rich organic matter as carbon source, metal vanadium salt as vanadium source, urea, ammonium carbonate, ammonium bicarbonate as nitrogen source, and so on. The carbon-coated VN nanoparticles are obtained by mechanical mixing and calcination in one step. The raw material of the invention is cheap, the synthesis method is simple and the controllability is high. The obtained VN is nanoparticles and coated with amorphous carbon layer, which improves the conductivity of the material. The carbon-coated VN nanomaterials prepared by this method have uniform chemical composition, high purity and crystallinity, and exhibit a certain catalytic activity for hydrogen production.
【技术实现步骤摘要】
一种碳包覆的氮化钒电催化剂、制备方法及应用
本专利技术属于电解水产氢催化剂
，具体涉及一种碳包覆的氮化钒电催化剂、制备方法及应用。
技术介绍
由于当今社会能源的短缺、环境污染急剧严重，氢气作为一种可储存、无污染、可再生的优质能源载体，已经受到广泛的研究和开发。电解水制氢法是一种操作简单、技术成熟的大规模的制氢方法；但是当前存在的最大问题是电能消耗大、产氢所需的最有效的催化剂Pt、Pd等贵金属及其合金价格昂，一些非贵金属催化剂包括镍或镍基材料、金属硫化物、硒化物、碳化物、氮化物、磷化物等已经被开发。因此开发价格低廉、含量丰富、催化活性高的催化剂来替代贵金属已经被广泛关注。氮化钒（VN）具有较高的机械强度，电子传输率，耐腐蚀性等优点，在化学、电池等领域具有广泛的应用，同事也是很有潜力的电催化材料，因此制备的碳包覆的氮化钒粉体在电催化产氢领域具有重要的意义。申请号为CN101717076A的中国专利“一种氮化钒的制备方法”将含钒化合物与有机氮化物混合，在含氮气体中煅烧，得到氮化钒。该方法原料准备的工序较复杂，制备过程需要控制的参数多，应用于超级电容器材料制备领域。...
【技术保护点】
1.一种碳包覆氮化钒电催化剂的制备方法，其特征在于，包括以下步骤：将金属钒盐、富碳有机物和氮源通过机械法均匀混合，所得混合物在惰性气氛保护下600～900℃煅烧2～3h，即可得到碳包覆的氮化钒。
【技术特征摘要】
1.一种碳包覆氮化钒电催化剂的制备方法，其特征在于，包括以下步骤：将金属钒盐、富碳有机物和氮源通过机械法均匀混合，所得混合物在惰性气氛保护下600～900℃煅烧2～3h，即可得到碳包覆的氮化钒。2.根据权利要求1所述的一种碳包覆的氮化钒电催化剂的制备方法，其特征在于，所述的金属钒盐为三氯化钒、偏钒酸铵、乙酰丙酮钒中的一种或多种。3.根据权利要求1所述的一种碳包覆的氮化钒电催化剂的制备方法，其特征在于，所述富碳有机物为三聚硫氰酸。4.根据权利要求1所述的一种碳包覆的氮化钒电催化剂的制备方法，其特征在于，氮源为尿素、碳酸铵、碳酸氢铵中的一种或多种。5.根据权利要求1所述的一种碳包覆的氮化钒电催化剂的制备方法，其特征在于，混合物在惰性气氛保...
【专利技术属性】
技术研发人员：曹丽云，王琳琳，冯亮亮，黄剑锋，冯李，徐瑞，何丹阳，巩颖波，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：陕西,61