The invention discloses a preparation method of NiV2S4 nanoparticle electrocatalyst and its application as an electrocatalytic cracking catalyst for aquatic hydrogen production. It belongs to the field of catalyst synthesis technology and application. The invention takes sulfur-rich organic matter as sulfur source, metal vanadium salt as vanadium source, metal nickel salt as nickel source, and through mechanical mixing and homogeneous calcination, NiV2S4 nanoparticles, homogeneous material chemical composition and electrocatalytic hydrogen-producing electrocatalysts with electrocatalytic activity in all PH electrolyte are obtained. The synthetic material of the invention is cheap, the synthetic method is simple, the production cost is low, and the controllability is high. NiV2S4 is a new type of electrocatalysts for hydrogen production from water pyrolysis, which exhibits certain hydrogen production catalytic activity in the range of total pH value (0 14).
【技术实现步骤摘要】
一种NiV2S4电催化剂及其制备方法
本专利技术属于水解电催化剂
，具体涉及一种NiV2S4电催化剂及其制备方法。
技术介绍
由于当今社会能源的短缺、环境污染急剧严重，氢气作为一种可储存、无污染、可再生的优质能源载体，已经受到广泛的研究和开发。电解水制氢法是一种操作简单、技术成熟的大规模的制氢方法；但是当前存在的最大问题是电能消耗大、产氢所需的最有效的催化剂Pt、Pd等贵金属及其合金价格昂，一些非贵金属催化剂包括镍或镍基材料、金属硫化物、硒化物、碳化物、氮化物、磷化物等已经被开发。因此开发价格低廉、含量丰富、催化活性高的催化剂来替代贵金属已经被广泛关注。所以研究成本低廉且能够有效降低析氢过电位的新颖阴极材料已成为研究热点。申请号为CN108325539A的中国专利“一种棒状自组装成花球状的钒修饰的Ni3S2电催化剂的合成方法”提出将洁净的泡沫镍浸入钒源浓度为5~30mm、钒源与硫源摩尔比为1:（0.5-12）的悬浊液中，进行微波溶剂热反应，充分反应后，得到棒状自组装成花球状的钒修饰的Ni3S2电催化剂材料。申请号为CN107117662A的中国专利“一种铝掺...
【技术保护点】
1.一种NiV2S4电催化剂的制备方法，其特征在于，包括以下步骤：将金属钒盐、镍源与富硫有机物放在研钵里进行研磨，得到均匀的混合物；将前述混合物在500‑900℃、惰性气氛下煅烧2‑3h，得到NiV2S4电催化剂。
【技术特征摘要】
1.一种NiV2S4电催化剂的制备方法，其特征在于，包括以下步骤：将金属钒盐、镍源与富硫有机物放在研钵里进行研磨，得到均匀的混合物；将前述混合物在500-900℃、惰性气氛下煅烧2-3h，得到NiV2S4电催化剂。2.根据权利要求1所述的一种NiV2S4电催化剂的制备方法，其特征在于，所述金属钒盐为三氯化钒、乙酰丙酮钒、偏钒酸铵中的一种或多种。3.根据权利要求1所述的一种NiV2S4电催化剂的制备方法，其特征在于，所述镍源为六水合硝酸镍。4.根据权利要求1所述的一种NiV2S4电催化剂的制备方法，其特征在于，所述富硫有机物为三聚硫氰酸、硫脲、硫代乙酰胺、硫粉中的一种或...
【专利技术属性】
技术研发人员：曹丽云，王琳琳，冯亮亮，黄剑锋，巩颖波，王潇，冯李，杜盈盈，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：陕西,61