The present invention relates to an explosion-proof aluminium alloy and its preparation method. An explosion-proof aluminium alloy is characterized by the composition of the following weight percentages: Fe 0.8-1.4%, Mn 0.4-0.6%, Si 0.04-0.14%, residual amount of Al and inevitable impurities. The aluminium alloy sheet provided by the invention has good elongation, high tensile strength and yield strength, improved plastic workability of the aluminium alloy and easy processing and forming. The invented explosion-proof aluminium alloy can be used not only for battery shell and explosion-proof cover plate, but also for making capacitor shell and explosion-proof cover plate, as well as for instruments and mobile devices used in explosive environment.
【技术实现步骤摘要】
一种防爆用铝合金及其制备方法
本专利技术涉及一种防爆用铝合金及其制备方法。
技术介绍
近些年来，各种高容量化的碱性电池、锂电池等广泛应用于电动自行车、电动汽车、电动工具、手提电脑、手机、摄像机和数码相机等移动式电器电子设备。但这种高容量电池密闭在一个封闭容器中引发的爆炸事故频频发生，这是因为电池使用不当，如碰撞、过充、短路、过热等，其内部会产生异常气体，使得起电池内部压力过大而出现爆炸的现象。为了防止高容量电池爆炸，通常电池外包装采用铝合金材料制作外壳和防爆盖板，其原因铝合金导热性好，在使用过程中即使与其他物体碰撞时，其变形热量能够大部分迅速地被附件吸收而散去，热磨削下的微粒所具有的热量较低，不会引起易爆环境下二次爆炸，具有很好的安全防爆性能。其次在电池过充、短路、过热时导致内部产生大量气体而引起电池内部压力骤然增高情况下，当压力超过防爆盖板上的防爆膜能够承受的预定压力时，防爆膜撕裂，电池泄压，从而避免爆炸。目前，高容量电池外壳和防爆盖板最常用的材料是3xxx系铝合金。但3xxx系铝合金制作防爆盖板存在材料强度过大，不能满足规定压力下泄压防爆。因此目前电池的防爆盖...
【技术保护点】
1.一种防爆用铝合金，其特征在于，由以下重量百分含量的成分组成：Fe 0.8～1.4％、Mn 0.4～0.6％，Si 0.04～0.14％，余量为Al和不可避免的杂质。
【技术特征摘要】
1.一种防爆用铝合金，其特征在于，由以下重量百分含量的成分组成：Fe0.8～1.4％、Mn0.4～0.6％，Si0.04～0.14％，余量为Al和不可避免的杂质。2.如权利要求1所述的防爆用铝合金，其特征在于，所述的不可避免的杂质单项含量小于0.002％，总和不超过0.015％。3.权利要求1或2所述的防爆用铝合金的制备方法，其特征在于，包括以下步骤：步骤1：采用铸造方式制备合金铸锭，在制造过程中控制成分的重量百分比含量为：Fe0.8～1.4％、Mn0.4～0.6％，Si0.04～0.14％，余量为Al和不可避免的杂质；步骤2：均匀化：将合金铸锭以15～40℃/h升温到450～550℃，保温4～10h冷却；步骤3：热轧变形：将均匀化后铸锭在400～550℃预热炉中进行5～60min预热处理，开轧温度400～550℃，终轧温度不低于350℃，道次压下量30～60％；步...
【专利技术属性】
技术研发人员：尤伟任，徐春，白清领，周冰，庞灵欢，徐海波，
申请(专利权)人：上海中天铝线有限公司，上海应用技术大学，江苏中天科技股份有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。