The present invention relates to a slag used for preparing high silicon manganese nitrogen stainless steel by electroslag remelting. Its characteristics are as follows: CaF2:50-70 parts, CaO:8-20 parts, Al2O3:5-20 parts, MgO:5-15 parts, SiO 2:1-10 parts and MnO 2:1-8 parts by weight. The high silicon manganese nitrogen-containing stainless steel alloy prepared by the slag has stable and controllable silicon and manganese elements, stable matrix structure, less harmful impurities and non-metallic inclusions, and optimized structure, which greatly improves the hot working performance and yield of the alloy, and obtains excellent mechanical properties and corrosion resistance.
【技术实现步骤摘要】
用于制备高硅锰含氮不锈钢的电渣重熔的渣料
本专利技术属于金属材料领域，特别涉及一种用于制备高硅锰含氮不锈钢的电渣重熔的渣料。
技术介绍
在奥氏体不锈钢中加入一定量的氮元素能起到适当降低钢中镍含量、稳定奥氏体基体，能明显提高钢的机械强度与耐腐蚀性能的作用，而锰同样是奥氏体形成元素，且有利于提高钢中氮的溶解度，可有效较低合金材料的成本，因此现代奥氏体不锈钢根据性能设计特点大多含有一定量的氮、锰。不锈钢中的硅是铁素体形成元素，能显著提高钢的强度、弹性极限、耐热性和高温强度，有利于提高耐腐蚀性、抗氧化、抗磨损等作用。高硅锰含氮的铬镍型奥氏体不锈钢，具有良好的横纵向强韧性匹配以及耐磨、耐腐蚀、抗空蚀和高温性能，在石油天然气开采、化工、水电、核电等重要工业领域得到了广泛应用，但由于硅含量较高，在凝固过程容易析出脆性的金属间相，比如σ，使得材料的热塑性变差，从而降低了成材率，提高了材料成本。这在大锭型(比如直径≥600mm)的工业生产过程尤为明显，非常不利于该材料推广应用。虽然通过电渣重熔可以提纯金属并使钢锭获得成分稳定可控、洁净组织均匀致密，但对于高硅和/或锰含氮型不锈钢来说...
【技术保护点】
1.用于制备高硅锰含氮不锈钢的电渣重熔的渣料，其特征在于，该渣料的各组成按重量份为：CaF2：50～70份、CaO：8～20份、Al2O3：5～20份、MgO：5～15份、SiO2：1～10份、MnO2：1～8份。
【技术特征摘要】
1.用于制备高硅锰含氮不锈钢的电渣重熔的渣料，其特征在于，该渣料的各组成按重量份为：CaF2：50～70份、CaO：8～20份、Al2O3：5～20份、MgO：5～15份、SiO2：1～10份、MnO2：...
【专利技术属性】
技术研发人员：刘海定，陈登华，王东哲，何曲波，王方军，刘应龙，吕晓敏，
申请(专利权)人：重庆材料研究院有限公司，
类型：发明
国别省市：重庆,50
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。