The invention discloses a reinforcing bar rust inhibitor based on radish extract and its preparation method and application, which comprises the following raw materials by quality calculation: 98%-100% radish extract and 0%-2% antiseptic additive. Compared with the existing technology, it has the following advantages: green and low-carbon material, low cost, wide material sources and large output, which is conducive to industrial production; avoiding the disadvantages of traditional nitrite pollution environment and complex preparation process of organic rust inhibitor; using the rust inhibitor components already contained in raw radish extract, the interaction between rust inhibitor components and steel bars makes the surface of steel bars. The existence of adsorption film inhibits the direct corrosion of chloride ions on steel bars; the prepared rust inhibitor has excellent rust-inhibiting effect; and the preparation method and application method are simple and has broad prospects.
【技术实现步骤摘要】
一种基于萝卜提取液的钢筋阻锈剂及制备方法与应用
本专利技术涉及钢筋阻锈剂领域，尤其涉及一种基于萝卜提取液的钢筋阻锈剂及制备方法与应用。
技术介绍
钢筋混凝土是一种重要的工程结构，在沿海环境、冬季除冰盐以及西部盐碱地等高氯盐环境中，钢筋混凝土面临氯盐的侵蚀破坏危险。氯离子通过迁移渗透对流扩散、毛细作用通过混凝土孔隙迁移到钢筋表面，当达到临界氯离子浓度时钢筋锈蚀反应加速，生成的膨胀性腐蚀产物会使得结构产生内应力，应力严重时会使得结构发生顺筋开裂。因而氯盐侵蚀破坏和提高钢筋混凝土结构的使用寿命是当前重要的研究热点。为了提高钢筋混凝土抗氯盐侵蚀性，研究学者已提出了许多方法，主要有通过提高混凝土的密实性、使用耐蚀和合金钢筋、使用钢筋阻锈剂和钢筋涂层、阴极保护法和混凝土再碱化等方法。其中阻锈剂由于使用便捷、成本低廉且能够起到对钢筋的长期保护作用而被广泛应用在工程实际中。但是现有的阻锈剂往往存在许多有待解决的问题，如以亚硝酸盐为代表的强氧化阳极型阻锈剂，阻锈效果虽然显著却对人类和环境具有很大的毒害，已被欧盟发达国家禁用。氨基醇型有机阻锈剂阻锈效率低制备复杂成本较高。因此寻找一种...
【技术保护点】
1.一种基于萝卜提取液的钢筋阻锈剂，其特征在于包括如下以质量计算的制备原料：98％‑100％萝卜提取液、防腐添加剂0％‑2％。
【技术特征摘要】
1.一种基于萝卜提取液的钢筋阻锈剂，其特征在于包括如下以质量计算的制备原料：98％-100％萝卜提取液、防腐添加剂0％-2％。2.根据权利要求1所述的基于萝卜提取液的钢筋阻锈剂，其特征在于：所述萝卜提取液的提取方法为首先取新鲜萝卜机械压碎，加入其质量5-15倍体积的酸溶液进行浸泡，浸泡完成后取上清液通过减压过滤装置过滤处理得滤液；再将滤液蒸馏处理后得所需萝卜提取液。3.根据权利要求2所述的基于萝卜提取液的钢筋阻锈剂，其特征在于：所述酸溶液为磷酸和硝酸。4.根据权利要求2所述的基于萝卜提取液的钢筋阻锈剂，其特征在于：所述浸泡的时间为1-10h。5.根据权利要求2所述的基于萝卜提取...
【专利技术属性】
技术研发人员：蒋林华，徐鹏，郭明志，陈晨，储洪强，
申请(专利权)人：河海大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。