The solid aldehyde remover for a car is composed of 30% mineral charcoal, 30% diatomite, 25% silica gel and 15% lemon granules. The particles of the solid aldehyde remover are all 2.5 to 3.5 mm. The diatomite granules are made of natural diatomite with a volume ratio of 50% and Yeguang mud. The silica gel granules are composed of natural diatomite with a volume ratio of 50% and Yeguang mud with a volume ratio of 50%. 35% amorphous silica gel and 65% activated bamboo charcoal are processed. The lemon granules are mixed with 10% lemon essential oil. The packaging bag for storing the solid aldehyde remover is made of printed canvas. The 500 grams of the solid aldehyde remover are stored in the packaging bag, and the color cotton braided tape in the middle of the tightening bag is tied into a bow to complete the packaging of a unit finished product. The outer side of the bag is pasted with a Zodiac cartoon sticker and a rubber pad on the bottom. The bag can be pasted on the front and rear panels of the car to form decorative ornaments.
【技术实现步骤摘要】
一种轿车除醛柠檬炭包的制作
本专利技术涉及一种轿车固体除醛剂的配制,尤其在于固体除醛剂包括纳米矿晶炭、柠檬粒、硅藻粒和硅胶粒,并采用适宜于轿车里使用的软包装,兼具装饰摆件的效果,一物二用。
技术介绍
目前,我国有关部门对轿车内苯醛类有害气体含量作了控制和检测标准,但轿车车厢内各种装饰材料要占其总面积85%以上,因此,有害挥发气体如甲醛、苯、二甲苯,TVOC、总有不同程度的挥发,它不仅影响人们的感官,产生不愉悦的心情,而且长久以往会对人体健康造成伤害,尤其是刚出厂的新车、在密闭环境下使用其伤害必然更甚,除了采用液体喷雾除醛剂外,采用固体除醛剂自动消除车厢内有害气体就成了人们的需求。现今国内市场上推出的汽车固体除醛剂品种十分繁多,都是采用多孔的具有吸附特性的物质加工成单质颗粒或复合颗粒,其包装一般采用无纺布制成圆形或矩形的布质包袋,或是采用带孔的塑料盒,置于车厢里使用,其效果有好有差,没有统一的标准。如何既能全面提升除醛功效,暨能散发有益清香,同时又能成为显示车主个性的车内摆设,乃是本专利技术所追求的目的。本专利技术固体除醛剂包含矿晶炭粒、硅藻粒、硅胶粒和柠檬粒,它们采用不同的原生态物质用物理方法复合配制,这些物质都是人们所公知的。其中,矿晶炭粒是用凹凸棒土、海泡石、电气石、活性炭天然矿物质经细化、煅烧工艺制成多孔的球状颗粒,由于其内部孔隙的孔径在0.27-0.98纳米之间,呈晶体排列,所以也称之为“纳米矿晶炭”,本专利技术中的矿晶炭粒直接采用由我国东莞某厂家产品,颗粒直径在2.5-3.5毫米之间。其中,硅藻粒是用天然硅藻土与叶广泥混合制成,在百度搜索引擎里可 ...
【技术保护点】
1.一种轿车除醛柠檬炭包的制作,其特征是:制作工艺如下:(1)采用我国东莞某厂家生产的矿晶炭粒,选取其颗粒直径在2.5‑3.5毫米之间备用;(2)将天然硅藻土、叶广泥各个粉碎,经烘干至含水率达90%以上,再投入蛋形球磨机研磨进一步细化达1000‑1200目之间,然后各按其两者总容积比例50%混合、并加水揉合,继续送入制丸机挤压成直径在2.5‑3.5毫米之间的硅藻粒,再自然干燥后备用;(3)用硅酸钠和硫酸反应,并经过老化、酸泡处理过程后制得非晶态硅胶,另外,将浙江遂昌产的活化竹炭粉碎后投入蛋形球磨机研磨、进一步细化达1600‑1800目后取出,然后取按硅胶和活化竹炭粉两者总容积比例的35%硅胶与按硅胶和活化竹炭粉两者总容积比例65%的活化竹炭粉投入搅拌机充分匀合,继续送入模压机固化形成直径在2.5‑3.5毫米之间硅胶粒备用;(4)取新鲜柠檬皮经过粉碎机切成4‑5毫米大小的颗粒,然后自然凉干或烘干制成含水率在90‑95%之间的柠檬胚粒,再将柠檬胚粒投入封闭的不锈钢转锅内,并按柠檬胚粒总容积的10%加入柠檬精油,充分拌合均匀制成3.5‑4.5柠檬粒备用,所述的柠檬精油从市场采购;(5)按总固 ...
【技术特征摘要】
1.一种轿车除醛柠檬炭包的制作,其特征是:制作工艺如下:(1)采用我国东莞某厂家生产的矿晶炭粒,选取其颗粒直径在2.5-3.5毫米之间备用;(2)将天然硅藻土、叶广泥各个粉碎,经烘干至含水率达90%以上,再投入蛋形球磨机研磨进一步细化达1000-1200目之间,然后各按其两者总容积比例50%混合、并加水揉合,继续送入制丸机挤压成直径在2.5-3.5毫米之间的硅藻粒,再自然干燥后备用;(3)用硅酸钠和硫酸反应,并经过老化、酸泡处理过程后制得非晶态硅胶,另外,将浙江遂昌产的活化竹炭粉碎后投入蛋形球磨机研磨、进一步细化达1600-1800目后取出,然后取按硅胶和活化竹炭粉两者总容积比例的35%硅胶与按硅胶和活化竹炭粉两者总容积比例65%的活化竹炭粉投入搅拌机充分匀合,继续送入模压机固化形成直径在2.5-3.5毫米之间硅胶粒备用;(4)取新鲜柠檬皮经过粉碎机切...