一种提钒冷却剂及其制备方法和提钒方法技术

本发明专利技术提供了一种提钒冷却剂，所述提钒冷却剂为渣铁。本发明专利技术采用渣铁作为提钒冷却剂，渣铁中的氧化亚铁能够改善熔渣的流动性，有利于脱磷，而且还能够降低铁水的温度，本发明专利技术提供的提钒冷却剂用于铁水中具有良好的提钒效果；同时本发明专利技术还能够使渣铁中的钒资源被回收利用，具有较好的经济效益。本发明专利技术还提供了一种提钒冷却剂的制备方法和提钒方法。

A Vanadium Extraction Coolant and Its Preparation Method and Vanadium Extraction Method

The invention provides a vanadium extracting coolant, which is slag iron. The present invention uses slag iron as vanadium extracting coolant, and ferrous oxide in slag iron can improve the fluidity of slag, is beneficial to dephosphorization, and can also reduce the temperature of molten iron. The vanadium extracting coolant provided by the present invention has good vanadium extracting effect in molten iron; at the same time, the present invention can make the vanadium resources in slag iron recovered and utilized, and has better economic benefits. The invention also provides a preparation method of vanadium extracting coolant and a vanadium extracting method.

【技术实现步骤摘要】
一种提钒冷却剂及其制备方法和提钒方法
本专利技术属于钢铁冶金
，尤其涉及一种提钒冷却剂及其制备方法和提钒方法。
技术介绍
攀西地区具有丰富的钒钛磁铁矿资源，其保有储量占全国储量的95％以上，攀钢自产的钒钛铁精矿每年700万吨左右，其他企业生产的钒钛铁精矿也在300万吨以上。钒钛铁精矿经高炉冶炼的铁水较普通矿冶炼所产生的铁水含钒量要高，达到0.3％以上。目前，转炉提钒的方法主要是加入提钒冷却剂，控制温度和吹炼时间来优化提钒操作。转炉提钒是一个放热过程，硅、钒、碳等元素氧化使转炉内熔池快速升温，而硅、锰的氧化发生在钒氧化之前，碳、钒的氧化温度大约在1385℃左右，要获得钒的高氧化率和收得率，在反应过程中需要通过加入提钒冷却剂来控制熔池的温度，以达到碳、钒转化的目的。铁水的冷却主要是通过向铁水中加入冷却剂实现的，目前现有技术常用的冷却剂有普通铁矿石、废钢、氧化铁皮、冷固球团等。由于钒钛铁水中含有钛，铁水在罐内温度降低时钛会析出，与铁水中C生成高熔点物质TiC粘附于铁罐壁，很难熔化，且与铁沟过渣和铁水在出铁过程中，铁水从铁沟内流入罐内过程中，铁水中的钒氧化成渣，造成粘结渣铁中钒含量高。本文档来自技高网...

【技术保护点】
1.一种提钒冷却剂，所述提钒冷却剂为渣铁。

【技术特征摘要】
1.一种提钒冷却剂，所述提钒冷却剂为渣铁。2.根据权利要求1所述的提钒冷却剂，其特征在于，所述提钒冷却剂的成分包括：40～80wt％的TFe；5～30wt％的FeO；0.01～0.1wt％的P；0.01～0.1wt％的S；1～8wt％的V2O5。3.根据权利要求1所述的提钒冷却剂，其特征在于，所述提钒冷却剂的粒度≤200mm。4.根据权利要求1所述的提钒冷却剂，其特征在于，所述提钒冷却剂的粒度为50～150mm。5.一种提钒冷却剂的制备方法，包括：将渣铁进行破碎、筛分和磁选，得到提钒冷却剂。6.根据权利要求5所述的方法，其特征在于，所述渣铁的成分包括：55～6...

【专利技术属性】
技术研发人员：蒋胜，王禹键，饶家庭，
申请(专利权)人：攀钢集团攀枝花钢铁研究院有限公司，
类型：发明
国别省市：四川,51