The invention relates to a one-component room temperature vulcanized organic silicone sealant with high temperature resistance and deacidification and a preparation method thereof. The sealant uses alpha, _-dihydroxy liquid polysiloxane as base gel, acyloxysilane crosslinking agent as crosslinking agent, modified silica as reinforcing filler, amphoteric metal oxide as high temperature degradation inhibitor, metal oxide as high temperature antioxidant, acyloxy group as crosslinking agent, etc. Silane, epoxy alkoxysilane or methacryloxysilane are used as tackifiers and organotin compounds as catalysts. The one-component room temperature vulcanized silicone sealant with high temperature and deacidification resistance has excellent high temperature and degradation resistance, high elongation at break and storage stability, and good adhesion performance to metal substrates.
【技术实现步骤摘要】
单组分耐高温脱酸型室温硫化有机硅密封胶及其制备方法
本专利技术是一种单组分耐高温脱酸型室温硫化有机硅密封胶及其制备方法，属于高分子材料及其生产
技术介绍
单组分缩合型室温硫化有机硅密封胶是最常见和用量最大的一种室温硫化有机硅密封胶，它使用方便，因此，在建筑、汽车、电子电器、机械、化工、轻工等领域获得广泛应用。单组分缩合型室温硫化有机硅密封胶，按交联剂不同可分为脱酮肟型、脱酸型、脱醇型、脱丙酮型和脱酰胺型等。当前在我国工程中实际应用的单组分室温硫化有机硅密封胶是脱酮肟型、脱酸型和脱醇型，其中，脱酸型单组分室温硫化有机硅密封胶对基材粘接性、耐高温性能和存储稳定性最好，但也存在对金属腐蚀性、高温降解方面的缺点。在一些耐高温要求苛刻和对乙酸腐蚀性不敏感的使用场合(如部分汽车和飞机的发动机部位)，单组分脱酸型室温硫化有机硅密封胶通过进一步抑制其高温降解，更能发挥其耐高温优势而得到应用。单组分脱酸型室温硫化有机硅密封胶具有优异的粘接性能和存储稳定性，因此，被大量的使用在建筑和装饰领域，其相关的研究也集中于对建筑和装饰领域的应用研究，如朱利明、俞虹、舒莺研究了白油对脱...
【技术保护点】
1.一种单组分耐高温脱酸型室温硫化有机硅密封胶，其特征在于：该密封胶的化学组成及质量份数为：
【技术特征摘要】
1.一种单组分耐高温脱酸型室温硫化有机硅密封胶，其特征在于：该密封胶的化学组成及质量份数为：所述的α,ω-二羟基液体聚硅氧烷为α,ω-二羟基聚二甲基硅氧烷或α,ω-二羟基聚甲基苯基硅氧烷，其粘度为5000～80000mPa·s；所述的交联剂为甲基三乙酰氧基硅烷、乙基三乙酰氧基硅烷或乙烯基三乙酰氧基硅烷其中的一种或两种混合物；所述的补强填料为改性气相法白炭黑；所述的高温降解抑制剂为氧化锌、氧化铝或三氧化铬；所述的高温抗氧剂为三氧化二铁、二氧化钛或氧化铈；所述的增粘剂为二叔丁氧基二乙酰氧基硅烷、γ-(2,3-环氧丙氧)丙基三...
【专利技术属性】
技术研发人员：孙全吉，王磊，任河，张鹏，王利娜，
申请(专利权)人：中国航发北京航空材料研究院，
类型：发明
国别省市：北京,11