The invention belongs to the application technology field of organic sulfur catalytic hydrolysis, in particular to a new method for preparing two-dimensional transition metal nanosheets and its application in the field of catalytic organic sulfur hydrolysis. The precursor KNb3O8 is obtained by mixing K2CO3 and Nb2O5, calcining, then dispersing the precursor into dilute nitric acid solution, stirring, washing to neutral, drying and grinding to obtain layered HNb3O8. The layered HNb3O8 and TBAOH were dissolved and diluted, then the dispersed liquid was stirred at room temperature, and the precipitate was removed by centrifugation to obtain Nb3O8.
【技术实现步骤摘要】
一种有机硫水解催化剂及其制备方法
本专利技术属于有机硫催化水解应用
，具体涉及一种制备过渡金属二维纳米片的新方法及其在催化有机硫水解领域的应用。
技术介绍
有机硫广泛存在于煤焦造气、炼厂气、克劳斯尾气以及油田气和天然气中，而羰基硫（COS）是工业气体中有机硫存在的主要形式。工业生产中微量的COS易引起催化剂中毒失活，并对工业生产的设备有腐蚀作用。此外，不经处理排放到大气中的COS能形成SO2，促进光化学反应，并最终转化为硫酸盐气溶胶，引起酸雨，带来严重的环境问题，因此，如何有效脱除COS是重要的研究课题。在酸性气体处理过程中，由于COS的化学活性比H2S小得多，其酸性和极性也弱于H2S，故而一般用于脱除H2S的方法并不能有效地完全脱除COS。目前脱除COS的技术有还原法、水解法、吸收法、光解法、吸附法和氧化法。而水解法是目前脱除COS最主要的方法，其具有转化率高、耗能低、副反应少的优点。水解法脱除COS的过程是：在催化剂的存在下，COS首先和水反应生成H2S，再用脱硫剂对H2S进行脱除，所以水解法脱除H2S的关键是水解催化剂的设计。目前已发展的水解催化剂主要...
【技术保护点】
1.一种有机硫水解催化剂的制备方法，其特征在于：以前驱体KNb3O8置于稀硝酸中制备层状HNb3O8；再通过层状HNb3O8和四丁基氢氧化铵，制备得到Nb3O8‑纳米片溶胶；Nb3O8‑的纳米片溶胶中，通过碱絮凝方法制备得到所述HNb3O8二维纳米片。
【技术特征摘要】
1.一种有机硫水解催化剂的制备方法，其特征在于：以前驱体KNb3O8置于稀硝酸中制备层状HNb3O8；再通过层状HNb3O8和四丁基氢氧化铵，制备得到Nb3O8-纳米片溶胶；Nb3O8-的纳米片溶胶中，通过碱絮凝方法制备得到所述HNb3O8二维纳米片。2.根据权利要求1所述的一种有机硫水解催化剂的制备方法，其特征在于：具体包括以下步骤：（1）将摩尔比为1:1.6-2.5的Nb2O5和K2CO3研磨均匀后加入无水乙醇，搅拌均匀后，烘干，然后在700-900℃焙烧15-25h，得到前驱体KNb3O8；（2）将前驱体KNb3O8分散入稀硝酸溶液中，搅拌5-10天，用去离子水洗涤至中性，烘干，研磨得到层状HNb3O8；（3）按摩尔比1:1.3-1.8称取层状HNb3O8和四丁基氢氧化铵，用水分散得分散液，再将分散液在常温下搅拌，离心除去沉淀物，得到Nb3O8-纳米片溶胶；（4）按体积比1:0.8-1.5将KOH溶液加入Nb3O8-的纳米片溶胶中，超声搅拌，将所得絮状物先用去离子水再用无水乙醇分别洗涤至中性，真空干燥，即得所述...
【专利技术属性】
技术研发人员：江莉龙，张林燕，沈丽娟，梁诗景，
申请(专利权)人：福州大学，
类型：发明
国别省市：福建,35