The invention discloses a graphene film and a preparation method thereof, in which the graphene film comprises a graphene film layer and a few graphene powders disorderly doped in the graphene film layer. The few graphene powders are bonded with the graphene film layer by a carbon covalent bond, and the few graphene powders are 1 3 layers of graphene. In the graphene film provided by the invention, the few layers of graphene powder can be disorderly bonded by carbon covalent bonds in the newly formed graphene film layer, thereby effectively improving the mechanical strength and conductivity of the graphene film.
【技术实现步骤摘要】
一种石墨烯薄膜及其制备方法
本专利技术涉及石墨烯领域，尤其涉及一种石墨烯薄膜及其制备方法。
技术介绍
石墨烯是一种新型的导热、导电优良的纳米材料，其单层厚度仅为0.35纳米。由于它的特殊性能，而被制作成各种各样的产品，其中最多的一种就是做成薄膜。传统的石墨烯薄膜做法是把石墨烯和树脂类或者其他具有黏结性的液体混合，再把它制作成各种规格的薄膜，所述薄膜可应用到导热、导电等地方，从而达到降低温度或者导电的作用。这种采用传统方法制备的石墨烯薄膜由于是用树脂类黏胶把石墨烯粉体粘合在一起，其中的石墨烯粉体与石墨烯粉体之间没有很好的结合，甚至没有任何联系，这导致制备的石墨烯薄膜机械强度差，且其导电导热性能也较差。因此，现有技术还有待于改进和发展。
技术实现思路
鉴于上述现有技术的不足，本专利技术的目的在于提供一种石墨烯薄膜及其制备方法，旨在解决现有石墨烯薄膜中的石墨烯粉体之间没有很好的结合，导致石墨烯薄膜机械强度差，以及导电导热性能均较差的问题。本专利技术的技术方案如下：一种石墨烯薄膜，其中，包括石墨烯膜层以及无序掺杂在所述石墨烯膜层内的少层石墨烯粉体，所述少层石墨烯粉体通过碳-碳...
【技术保护点】
1.一种石墨烯薄膜，其特征在于，包括石墨烯膜层以及无序掺杂在所述石墨烯膜层内的少层石墨烯粉体，所述少层石墨烯粉体通过碳‑碳共价键与所述石墨烯膜层结合，所述少层石墨烯粉体为1‑3层的石墨烯。
【技术特征摘要】
1.一种石墨烯薄膜，其特征在于，包括石墨烯膜层以及无序掺杂在所述石墨烯膜层内的少层石墨烯粉体，所述少层石墨烯粉体通过碳-碳共价键与所述石墨烯膜层结合，所述少层石墨烯粉体为1-3层的石墨烯。2.一种石墨烯薄膜的制备方法，其特征在于，包括步骤：提供一种少层石墨烯粉体，所述少层石墨烯粉体为1-3层的石墨烯；将所述少层石墨烯粉体预先均匀铺在平整的金属基材表面；将表面铺有少层石墨烯粉体的金属基材放入CVD反应腔室中，通入甲烷和保护气体，在预定气压下加热至预定温度使甲烷分裂成碳原子并溶入到所述金属基材中；对所述金属基材进行退火处理，使溶入到金属基材中的碳原子析出并与金属基材表面的少层石墨烯粉体通过碳-碳共价键结合，在所述金属基材表面生成完整的石墨烯薄膜。3.根据权利要求2所述石墨烯薄膜的制备方法，其特征在于，所述金属基材为铜箔或铝箔中的一种。4....
【专利技术属性】
技术研发人员：柯良节，
申请(专利权)人：天元羲王控股有限公司，
类型：发明
国别省市：中国香港,81