The invention provides a surface passivation treatment solution for metal stamping parts, which comprises the following components: inorganic corrosion inhibitor 5 20g/L, rare earth salt 2 15g/L, organic acid 0.5 2.5g/L, and activator 0.5 2.5g/L. Preferably, the inorganic corrosion inhibitor is molybdate. Preferably, the rare earth salts are ammonium cerium nitrate, ammonium hydroxide, cerium acetate, samarium oxide, lanthanum nitrate and zirconium nitrate. Preferably, the organic acid is carboxylic acid. Preferably, the active agents are metal oxides, hydroxides and basic carbonates. The formulation of the invention is simple and practical, without chromate, safe, environmental protection and pollution, and the passive film generated has strong adhesion ability, compact film layer and good scratch resistance.
【技术实现步骤摘要】
一种五金冲压件表面钝化处理液
本专利技术涉及五金冲压件表面处理技术，具体涉及一种五金冲压件表面钝化处理液。
技术介绍
钝化处理是化学清洗中最后一个工艺步骤，是关键一步，其目的是为了材料的防腐蚀。如锅炉经酸洗、水冲洗、漂洗后，金属表面很清洁，非常活化，很容易遭受腐蚀，所以必须立即进行钝化处理，使清洗后的金属表面生成保护膜，减缓腐蚀。目前常用钝化液是铬酸盐，铬对环境污染严重。由于风化作用进入土壤中的铬，容易氧化成可溶性的复合阴离子,然后通过淋洗转移到地面水或地下水中。土壤中铬过多时，会抑制有机物质的硝化作用，并使铬在植物体内蓄积。三价铬和六价铬对水生生物都有致死作用。水体中的三价铬主要被吸附在固体物质上而存在于沉积物中；六价铬则多溶于水中。六价铬在水体中是稳定的，但在厌氧条件下可还原为三价铬。三价铬的盐类可在中性或弱碱性溶液中水解，生成不溶于水的氢氧化铬而沉入水底。天然水中一般仅含微量的铬，通过河流输送入海，沉于海底。海水中的铬含量不到1ppb。据试验，水中含铬在1ppm时可刺激作物生长，1～10ppm时会使作物生长减缓，到100ppm时则几乎完全使作物停止生长，濒于...
【技术保护点】
1.一种五金冲压件表面钝化处理液，其特征在于，包括如下组分：无机缓蚀剂5‑20g/L，稀土盐2‑15g/L，有机酸0.5‑2.5g/L，活性剂0.5‑2.5g/L。
【技术特征摘要】
1.一种五金冲压件表面钝化处理液，其特征在于，包括如下组分：无机缓蚀剂5-20g/L，稀土盐2-15g/L，有机酸0.5-2.5g/L，活性剂0.5-2.5g/L。2.根据权利要求1所述的一种五金冲压件表面钝化处理液，其特征在于，所述无机缓蚀剂为钼酸盐。3.根据权利要求1所述的一种五金冲压...
【专利技术属性】
技术研发人员：易巧英，宋文选，朱世勇，
申请(专利权)人：南京海印通信设备有限公司，
类型：发明
国别省市：江苏,32