The flash-firing preparation method of ternary lithium battery cathode material of the invention comprises the following steps: (1) homogeneous mixing of nano-scale oxide materials and dry pressing forming to obtain green billet; (2) placing the green billet in a tubular furnace and heating it to 200-600 degrees Celsius; (3) using electrode materials to hold both sides of the green billet through direct current, and controlling the voltage to rise linearly from 0V to 100V/s at a speed of 20-100V/s. Flash phenomenon occurs at about 60-100V; (4) control current to below 60A, constant current; lasts for 5-8 minutes; (5) reduce temperature to room temperature to obtain ternary lithium battery cathode material sintered body; (6) crush sintered body to 200 mesh powder to obtain products.
【技术实现步骤摘要】
三元锂电池正极材料的闪烧制备方法
本专利技术涉及机械电子产品制备技术，具体的，其展示一种三元锂电池正极材料的闪烧制备方法。
技术介绍
三元锂电池正极材料具有高比容量，长循环寿命，低毒和廉价的特点，由于镍，锰，钴三种元素之间具有良好的协同效应，因此具有优良的综合性能，从而受到了锂电池行业的广泛关注。但是其制备方法存在能耗高，性能不稳定的缺陷。目前广泛使用的制备方法包括共沉淀法，高温固相烧结法和喷雾干燥法。一般首先采用共沉淀法，得到原料混合均匀，材料粒径均一的前驱体，然后经过高温煅烧得到表面规整的三元材料。喷雾干燥法过程简单，利用雾化法使原料溶液直接形成粉体，但材料形貌难以控制。三元材料的晶粒尺寸和微观结构决定了其性能，因此需要通过制备工艺的改进来提升性能，降低成本。因此，有必要提供一种三元锂电池正极材料的闪烧制备方法来解决上述问题。
技术实现思路
本专利技术的目的是提供一种三元锂电池正极材料的闪烧制备方法。一种三元锂电池正极材料的闪烧制备方法，步骤如下：（1）将纳米级的氧化物原料均匀混合后干压成型得到素坯；（2）将素坯置于管式炉中加热到200～600摄氏度；（3）使用电...
【技术保护点】
1.一种三元锂电池正极材料的闪烧制备方法，其特征在于：步骤如下：（1）将纳米级的氧化物原料均匀混合后干压成型得到素坯；（2）将素坯置于管式炉中加热到200～600摄氏度；（3）使用电极材料夹持素坯两侧，通以直流电，控制电压从0V开始以20～100V／s的速度线性上升，直至在约60～100V时发生闪光现象；（4）控制电流降至60A以下，恒定电流；持续5～8分钟；（5）降温至室温，得到三元锂电池正极材料烧结体；（6）将烧结体粉碎至200目粉体，得到产品。
【技术特征摘要】
1.一种三元锂电池正极材料的闪烧制备方法，其特征在于：步骤如下：（1）将纳米级的氧化物原料均匀混合后干压成型得到素坯；（2）将素坯置于管式炉中加热到200～600摄氏度；（3）使用电极材料夹持素坯两侧，通以直流电，控制电压从0V开始以20～100V／s的速度线性上升，直至在约60～100V时发生闪光现象；（4）控制电流降至60A以下，恒定电流；持续5～8分钟；（5）降温至室温，得到三元锂电池正极材料烧结体；（6）将烧结体粉碎至200目粉体，得到产品。2.根据...
【专利技术属性】
技术研发人员：周晖雨，贾建平，贾建顺，
申请(专利权)人：苏州山人纳米科技有限公司，
类型：发明
国别省市：江苏,32