The invention relates to a green environmental protection thermoplastic halogen-free cable material with high strength, high elongation and low smoke, which is made up of 45-60 parts of linear low density polyethylene, 15-23 parts of monoalkoxytitanate, 14-23 parts of ethylene-vinyl acetate copolymer, 3-7 parts of compatibilizer, 2-4 parts of antioxidant, 1-2 parts of flame retardant and 30-45 parts of inorganic filler. The mechanical thermoplasticity of cable material can be greatly improved by using special compatibilizer formula. The thermoplastic halogen-free cable material of the invention has high strength, high elongation and low smoke. By using special composite flame retardant and compound antioxidant formula, the flame retardancy of the cable material is greatly improved besides maintaining its good mechanical properties.
【技术实现步骤摘要】
一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料
本专利技术特别涉及一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料。
技术介绍
传统电缆的最外层的主要材料为聚氯乙烯，即PVC（Polyvinylchloridepolymer），且含有卤系阻燃剂。聚氯乙烯为基材的电缆料虽然存在价格低、阻燃性好和加工性能好等优势；但是该材料在燃烧时发烟量大，产生大量腐蚀性气体和有毒气体（如氯气、HBr等），对灭火及人员逃生带来了不利影响，使得火灾救援更加困难。同时释放的腐蚀性气体，使得火灾现场的电器遭到腐蚀而被破坏。另外，卤系阻燃剂在生产、运输、储藏、废弃产品的回收过程中会毒性积累以及产生致癌物质。因此，研发出一种绿色环保电缆料越来越受到人们的关注。
技术实现思路
本专利技术针对上述问题提出了一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料。具体的技术方案如下：一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料，其特征在于，是由下列重量份的原料配比制成：线性低密度聚乙烯45～60份单烷氧基钛酸酯15～23份乙烯-醋酸乙烯共聚物14～23份相容剂3～7份抗氧剂2～4...
【技术保护点】
1.一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料，其特征在于，是由下列重量份的原料配比制成：线性低密度聚乙烯 45～60份单烷氧基钛酸酯 15～23份乙烯‑醋酸乙烯共聚物 14～23份相容剂 3～7份抗氧剂 2～4份阻燃剂 1～2份无机填料 30～45份。
【技术特征摘要】
1.一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料，其特征在于，是由下列重量份的原料配比制成：线性低密度聚乙烯45～60份单烷氧基钛酸酯15～23份乙烯-醋酸乙烯共聚物14～23份相容剂3～7份抗氧剂2～4份阻燃剂1～2份无机填料30～45份。2.如权利要求1所述的一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料，其特征在于，所述线性低密度聚乙烯熔融指数为4～6g/10min。3.如权利要求1所述的一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料，其特征在于，所述相容剂为POE-g-MAH(马来酸酐官能团接枝乙烯-辛烯共聚物)与EVA-g-MAH(马来酸酐官能团接枝乙烯-醋酸乙烯共聚物)的混合物，混合重量比例为POE-g-MAH︰EVA-g-MAH=2:3。4.如权利要求1所述的一种绿色环保的90℃高强度高伸长率热塑性低烟无卤电缆料，其特征在于，所述乙烯-醋酸乙烯共聚物中...