一种快硬水泥制造技术

本发明专利技术公开了一种快硬水泥，由以下原料按照重量百分比组成：石膏2％，硼砂0.5％，矿物掺合料15％，硫铝盐酸水泥82.5％；所述矿物掺合料按照组份组成：页岩石粉15重量份；天然砂55重量份，水泥熟料12重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份。本发明专利技术能有效提高水泥的抗压强度和早期强度，同时充分利用了工业废渣，大大降低了生产成本，有效改善硫铝盐酸水泥的性能。

A Fast Hardening Cement

The invention discloses a fast-hardening cement, which consists of gypsum 2%, borax 0.5%, mineral admixture 15%, sulphur-aluminium hydrochloric acid cement 82.5% according to weight percentage. The mineral admixture is composed of 15 weight parts of shale powder, 55 weight parts of natural sand, 12 weight parts of cement clinker, 15 weight parts of silica fume, 12 weight parts of kaolin powder and 15 weight parts of fly ash. Calcium sulfate 2 parts by weight. The invention can effectively improve the compressive strength and early strength of cement, make full use of industrial waste residue, greatly reduce production cost, and effectively improve the performance of sulphoaluminium hydrochloric acid cement.

【技术实现步骤摘要】
一种快硬水泥
本专利技术涉及建筑材料
，具体涉及一种早强快硬水泥。
技术介绍
水泥，是粉状水硬性无机胶凝材料，其加水搅拌后成浆体，能在空气中硬化或者在水中更好的硬化，并能把砂、石等材料牢固地胶结在一起，广泛应用于土木建筑、水利、国防等工程。硫铝盐酸水泥是一种高效特种水泥，具有快硬，早强，高强，低碱性，耐腐蚀等特点，但也存在早起水化热高，凝结时间果断，后期强度有不同程度的倒缩等问题。
技术实现思路
本专利技术的目的是提供一种硫铝盐酸水泥，以解决硫铝酸盐水泥存在的问题。一种快硬水泥，由以下原料按照重量百分比组成：石膏2％，硼砂0.5％，矿物掺合料15％，硫铝盐酸水泥82.5％；所述矿物掺合料按照组份组成：页岩石粉15重量份；天然砂55重量份，水泥熟料12重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份。本专利技术有益效果：本专利技术能有效提高水泥的抗压强度和早期强度，同时充分利用了工业废渣，大大降低了生产成本，有效改善硫铝盐酸水泥的性能。具体实施方式实施例1一种快硬水泥，由以下原料按照重量百分比组成：石膏2％，硼砂0.5％，矿物掺合料15％，硫铝盐酸水泥82.5％；所述矿物掺合料按照组份组成：页岩石粉15重量份；天然砂55重量份，水泥熟料12重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份。以上所述仅为本专利技术的优选实施例而已，并不用于限制本专利技术，对于本领域的技术人员来说，在本专利技术的精神和原则内可以有各种更改和变化，这些等同的变型或替换等，均包含在本专利技术的保护范围之内。

【技术保护点】
1.一种快硬水泥，其特征在于，由以下原料按照重量百分比组成：石膏2％，硼砂0.5％，矿物掺合料15％，硫铝盐酸水泥82.5％；所述矿物掺合料按照组份组成：页岩石粉15重量份；天然砂55重量份，水泥熟料12重量份，硅灰15重量份，高岭土粉12重量份，粉煤灰15重量份，硫酸钙2重量份。

【技术特征摘要】
1.一种快硬水泥，其特征在于，由以下原料按照重量百分比组成：石膏2％，硼砂0.5％，矿物掺合料15％，硫铝盐酸水泥82.5％；所述矿物掺合料...

【专利技术属性】
技术研发人员：陆远林，
申请(专利权)人：扬州佳奕金属材料有限公司，
类型：发明
国别省市：江苏,32