铝铜钎料、焊环与管材制造技术

本发明专利技术提供了铝铜钎料、焊环与管材。该铝铜钎料包括：铝、铜和稀土金属。在该铝铜钎料中，铝、铜、以及稀土金属会形成三元化合物，铝与铜、稀土金属三者之间相互配合发生协同作用，可以使得所述铝铜钎料的熔点较低，且具有较高抗拉强度和屈服强度，力学性能优异，抗腐蚀性能好，进而在使用该铝铜钎料进行焊接时，焊缝牢固、强度高、表面光滑、气孔较少，可达到焊接管材的使用要求，焊接效果好，且特别适合用于焊接以形成铜铝复合管。

Aluminum-Copper Brazing Alloy, Welding Ring and Pipe Material

The invention provides an aluminium-copper brazing alloy, a welding ring and a pipe. The aluminium-copper solder comprises aluminium, copper and rare earth metals. Aluminum, copper and rare earth metals will form ternary compounds in the Al-Cu solder. The synergistic effect between Al and copper and rare earth metals can make the Al-Cu solder have lower melting point, higher tensile strength and yield strength, excellent mechanical properties and good corrosion resistance. When the Al-Cu solder is used for welding, the weld seam is firm and strong. With high strength, smooth surface and less pore, it can meet the requirements of welded pipes, and has good welding effect. It is especially suitable for welding to form copper-aluminium composite pipes.

【技术实现步骤摘要】
铝铜钎料、焊环与管材
本专利技术涉及材料
，具体地，涉及铝铜钎料、焊环与管材。
技术介绍
在相关技术中，用于将管材进行焊接的钎料可以选用铜锡钎料。然而，采用铜锡钎料进行焊接时，由于管材表面上通常会存在一层氧化膜，使得锡与管材无法较好地结合，尤其是对于含有金属铝的管材，使用铜锡钎料进行钎焊，铜锡钎料与含有铝的管材之间不存在相互结合的作用，导致钎焊时的焊缝十分不牢固，钎焊效果较差。因而，现有的用于管材焊接的钎料的相关技术仍有待改进。
技术实现思路
本专利技术旨在至少在一定程度上解决相关技术中的技术问题之一。专利技术人经过对钎料中的各个组分、制备工艺的大量深入研究后惊喜地发现，在含有稀土金属的铝铜钎料中，铝、铜、以及稀土金属会形成三元化合物，铝与铜、稀土金属三者之间相互配合发生协同作用，可以使得所述铝铜钎料的熔点较低，且具有较高抗拉强度和屈服强度，力学性能优异，抗腐蚀性能好，进而在使用该铝铜钎料进行焊接时，焊缝牢固、强度高、表面光滑、气孔较少，且铝、铜、以及稀土金属形成三元化合物，即使在表面存在氧化膜时也可以使得钎料与管材的结合力强，相容性好，可达到焊接管材的使用要求，焊接效果好，且特别本文档来自技高网...

【技术保护点】
1.一种铝铜钎料，其特征在于，包括：铝、铜和稀土金属。

【技术特征摘要】
1.一种铝铜钎料，其特征在于，包括：铝、铜和稀土金属。2.根据权利要求1所述的铝铜钎料，其特征在于，所述稀土金属包括镧、铈、镨和钕中的至少一种。3.根据权利要求1所述的铝铜钎料，其特征在于，所述稀土金属包括镧、铈、镨和钕中的至少两种。4.根据权利要求1所述的铝铜钎料，其特征在于，不含锡。5.根据权利要求1所述的铝铜钎料，其特征在于，进一步包括：磷和KAlF4。6.根据权利要求5所述的铝铜钎料，其特征在于，包括：72.25重量份～81.84重量份的所述铝；2.5重量份～4.5重量份的所述铜；5.5重量份～8.0重量份的所述磷；10重量份～15重量份的所述KAlF4...

【专利技术属性】
技术研发人员：要东明，
申请(专利权)人：广东美的制冷设备有限公司，美的集团股份有限公司，
类型：发明
国别省市：广东,44