The invention discloses a soybean glue and its preparation method, as well as a method for producing light board by using soybean glue, which relates to an adhesive based on protein or its derivatives, and the method field of making plywood by using the adhesive, in order to solve the defects of formaldehyde release from the trialdehyde glue used in existing plates and pose a threat to human health. The soybean gum comprises soybean meal, water and composite modified crosslinking agent, which is prepared in pure alkaline environment. In the process of making light board with soybean gum, the pre-pressing unit pressure is 0.6 0.8 MPa, the hot-pressing unit pressure is 0.4 0.6 MPa, and the density of the prepared light board is less than 400 kg/m.
【技术实现步骤摘要】
大豆胶及其制备方法以及利用大豆胶生产轻质板的方法
本专利技术涉及一种基于蛋白质或其衍生物的粘合剂，以及使用该粘合剂制作胶合板的方法，具体地说，涉及一种大豆胶及其制备方法以及利用大豆胶生产轻质板的方法。
技术介绍
胶合板的使用非常广泛，但因其含有甲醛，成为制约其应用的一大难题。胶合板中所含的甲醛除微量来自于木材本身外，其他主要来源于胶粘剂。目前使用比较多的胶粘剂为“三醛胶”，即：脲醛树脂、酚醛树脂和三聚氰胺甲醛树脂(或三聚氰胺-尿素-甲醛共缩聚树脂)，三醛胶因甲醛含量高，容易导致室内空气中甲醛含量长期超标，对人体健康造成威胁。因此，环保型胶粘剂逐渐引起各国工业界的重视。蛋白胶粘剂是以蛋白质作为主要原料的一类天然胶粘剂的总称，可分为动物蛋白胶粘剂和植物蛋白胶粘剂，属于植物蛋白胶粘剂的大豆胶粘剂因能够替代化石资源，原料来源丰富，价格低廉，安全环保等原因显示出了较大的发展潜力，虽然大豆胶粘剂存在粘结强度低、耐水性差等缺陷，但因全球石油资源的有限性和环境污染问题日益受到关注等原因，使得工业应用中重新考虑环境友好型的天然胶粘剂，大豆蛋白胶粘剂再次成为研究热点。最早的大豆蛋白胶...
【技术保护点】
1.一种大豆胶，其特征在于，包括如下重量份的组分：豆粕20‑40份，水40‑80份，复合改性交联剂20‑30份；所述复合改性交联剂包括以下重量份的有效组分：2,3‑二巯基丙磺酸钠10‑20份，酰胺类聚合物30‑40份，硫酸锌3‑9份、硝酸铝1‑3份、十二烷基硫酸钠2‑7份、单宁5‑10份。
【技术特征摘要】
1.一种大豆胶，其特征在于，包括如下重量份的组分：豆粕20-40份，水40-80份，复合改性交联剂20-30份；所述复合改性交联剂包括以下重量份的有效组分：2,3-二巯基丙磺酸钠10-20份，酰胺类聚合物30-40份，硫酸锌3-9份、硝酸铝1-3份、十二烷基硫酸钠2-7份、单宁5-10份。2.根据权利要求1所述的大豆胶，其特征在于，所述酰胺类聚合物为聚酰胺多胺环氧氯丙烷或两性聚丙烯酰胺。3.根据权利要求1所述的大豆胶，其特征在于，所述大豆胶还包括氟化钠，氟化钠的用量为1-2份。4.一种权利要求1或2所述的大豆胶的制备方法，其特征在于，包括以下步骤：(1)水中加入氢氧化钠搅拌，调节pH＝9-11，加入豆粕搅拌处理1-2h；(2)继续搅拌，在搅拌过程中加入2，3-二巯基丙磺酸钠，搅拌0.8-1.5h后加入酰胺类聚合物，继续搅拌0.5-1h；在搅拌过程中维持pH＝9-11；(3)加入硫酸锌和硝酸铝继续搅拌，并维持pH＞7；(4)加入十二烷基硫酸钠，继续搅拌，并维持pH＞7；(5)加入单宁，继续搅拌...
【专利技术属性】
技术研发人员：宋启华，
申请(专利权)人：山东绿点环保材料有限公司，
类型：发明
国别省市：山东,37