The present invention provides an adhesive for bonding aluminium box igniter to carbon fiber material. Its components include epoxy resin E_51 of 100-120 weight parts, epoxy resin 711 of 80-100 weight parts, mica powder of 100-150 weight parts, aluminium oxide of 30-40 weight parts, GX 550 of 8-10 weight parts, JLY_121 polysulfide rubber of 50-60 weight parts and polycondensation amine of 80-90 weight parts. The epoxy resin is used as the basic component, and the anticipated service performance is obtained by adding curing agent, toughening agent, filler and other components, which can improve the bonding strength after curing, reduce the curing time and ensure the safe operation of the initiating device.
【技术实现步骤摘要】
一种铝盒点火器与碳纤维材料粘接用胶粘剂
本专利技术涉及低温固化条件下，点火器铝盒与碳纤维难粘复合材料的粘接技术。
技术介绍
点火器装置是固体火箭发动机中的一个重要部件。铝盒点火器与碳纤维材料粘接的产品结构由收敛段内衬和带药点火器装置组成。收敛段内衬粘接面为难粘接碳纤维复合材料，点火器装置粘接面为铝合金，粘接面为回转锥面体配合，两者使用胶粘剂进行粘接。粘接方式的连接结构重量轻，可以连接不同材质的材料。随着固体火箭发动机性能的提高，受发动机大型化的影响，点火器与收敛段内衬的粘接界面的复杂程度不断提高，收敛段内衬与铝盒点火器配合间隙差异很大，粘接间隙差异可以达到十倍以上，而且粘接过程中点火器装置的点火孔中不能有胶粘剂存在。为满足点火器装置的粘接要求，胶粘剂首先要对被粘零件具有良好的浸润性；其次，胶粘剂固化过程使用接触压力即可；再次，粘接剂具有较好的触变特性，既可以顺利填充0.01mm左右的配合间隙，又能填充局部0.2mm～0.3mm配合间隙，固化过程中不会出现流胶现象。受固体火箭发动机点火装置的影响，粘接剂需要在室温或稍高于室温的条件下固化，无需复杂的加热加压设备。粘接...
【技术保护点】
1.一种铝盒点火器与碳纤维材料粘接用胶粘剂，其特征在于：组分包括100～120重量份的环氧树脂E‑51、80～100重量份的环氧树脂711、100～150重量份的云母粉、30～40重量份的氧化铝、8～10重量份的GX‑550、50～60重量份的JLY‑121聚硫橡胶和80～90重量份的105缩胺。
【技术特征摘要】
1.一种铝盒点火器与碳纤维材料粘接用胶粘剂，其特征在于：组分包括100～120重量份的环氧树脂E-51、80～100重量份的环氧树脂711、100～150重量份的云母粉、30～40重量份的氧化铝、8～10重量份的GX-550、50～60重量份的JLY-121聚硫橡胶和80～90重量份的105缩胺。2.根据权利要求1所述的铝盒点火器与碳纤维材料粘接用胶粘剂，其特征在于：使用前先对点火器装置粘接面进行喷砂处理，在收敛段内衬粘接面使用砂纸进行打磨，使用丙酮清洗粘接面后在粘接面均匀涂抹铝盒点火器与碳纤维材料粘接用胶粘剂，并清理多余铝盒点火器与碳纤维材料粘接用胶粘剂...
【专利技术属性】
技术研发人员：王纪霞，包乐，张海鹏，张权，张新航，赵荣，李晓奋，张崇耿，