The invention discloses a battery diaphragm masterbatch based on modified resin, which comprises the following raw materials according to weight: polyurethane resin 52_67, purple cloud extract 10_18, colloidal silica 21_35, glycerol 3_7, fluorite powder 5_11, Polydimethyldiallyl ammonium chloride 1_4, lubricant 0.5_1.6. The present invention has reasonable composition ratio, is made of modified polyurethane resin as the main material, supplemented by various auxiliary materials, and has excellent mechanical properties. As the master material of battery separator, the present invention can effectively improve the quality of finished products, has broad market prospects and high application value.
【技术实现步骤摘要】
一种基于改性树脂的电池隔膜母料及其制备方法
本专利技术涉及电子材料领域，具体是一种基于改性树脂的电池隔膜母料及其制备方法。
技术介绍
锂电池的结构中，隔膜是关键的内层组件之一。隔膜的性能决定了电池的界面结构、内阻等，直接影响电池的容量、循环以及安全性能等特性，性能优异的隔膜对提高电池的综合性能具有重要的作用。隔膜的主要作用是使电池的正、负极分隔开来，防止两极接触而短路，此外还具有能使电解质离子通过的功能。隔膜材质是不导电的，其物理化学性质对电池的性能有很大的影响。电池的种类不同，采用的隔膜也不同。对于锂电池系列，由于电解液为有机溶剂体系，因而需要有耐有机溶剂的隔膜材料，一般采用高强度薄膜化的聚烯烃多孔膜。现有的电池隔膜大多存在不同程度上的缺陷，究其原因在于电池隔膜的母料性能不佳，尤其在力学性能上的表现不甚理想。
技术实现思路
本专利技术的目的在于提供一种基于改性树脂的电池隔膜母料及其制备方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种基于改性树脂的电池隔膜母料，包括以下按照重量份的原料：聚氨酯树脂52-67份、紫云提取物10-18...
【技术保护点】
1.一种基于改性树脂的电池隔膜母料，其特征在于，包括以下按照重量份的原料：聚氨酯树脂52‑67份、紫云提取物10‑18份、胶态二氧化硅21‑35份、甘油3‑7份、萤石粉5‑11份、聚二甲基二烯丙基氯化铵1‑4份、润滑剂0.5‑1.6份。
【技术特征摘要】
1.一种基于改性树脂的电池隔膜母料，其特征在于，包括以下按照重量份的原料：聚氨酯树脂52-67份、紫云提取物10-18份、胶态二氧化硅21-35份、甘油3-7份、萤石粉5-11份、聚二甲基二烯丙基氯化铵1-4份、润滑剂0.5-1.6份。2.根据权利要求1所述的基于改性树脂的电池隔膜母料，其特征在于，包括以下按照重量份的原料：聚氨酯树脂57-62份、紫云提取物13-15份、胶态二氧化硅26-30份、甘油4-6份、萤石粉7-9份、聚二甲基二烯丙基氯化铵1.5-3.5份、润滑剂0.7-1.4份。3.根据权利要求2所述的基于改性树脂的电池隔膜母料，其特征在于，包括以下按照重量份的原料：聚氨酯树脂59份、紫云提取物14份、胶态二氧化硅29份、甘油5份、萤石粉8份、聚二甲基二烯丙基氯化铵3份、润滑剂1.1份。4.根据权利要求1所述的基于改性树脂的电池隔膜母料，其特征在于，所述紫云提取物的制备方法如下：将采摘的紫云花清洗干净，剔除杂物和腐烂变质部分，放入蒸馏釜中，加入适量水进行蒸馏，收集馏液，往馏液中加入氯化钠，充分搅拌，静置，分离出油分，将分离出的油分再次加入饱和的氯化钠溶液中，充分搅拌，静置，再次分离出油分即得...