The invention relates to the technical field of lens, and specifically discloses a preparation method of high crack resistance lens, which includes the following steps: S1, heating polycarbonate to melting state, adding calcium tungstate and cotton fibers under stirring, continuing heat preservation and stirring, cooling, and obtaining modified polycarbonate; S2, heating modified polycarbonate and polyurethane to melting state respectively, mixing evenly, and then placing them in the mirror. Composite film is formed on the surface of the optical roller with micro-structure, and the composite film is hot pressed into the mirror through the optical roller with micro-structure of the mirror. S3. After cooling the mirror, the upper and lower surfaces of the mirror are coated and trimmed to obtain a high crack-resistant lens. The lens obtained by the invention has excellent crack resistance.
【技术实现步骤摘要】
一种高抗裂透镜的制备方法
本专利技术涉及透镜
，具体涉及一种高抗裂透镜的制备方法。
技术介绍
透镜是根据光的折射规律制成的，是由透明物质制成的一种光学元件。透镜所成的像有实像也有虚像。透镜可广泛应用于安防、车载、数码相机、激光、光学仪器等各个领域，随着市场不断的发展，透镜技术也越来越应用广泛。但是现有的透镜抗裂性能不高，难以满足市场的需求，使企业效益不高。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种高抗裂透镜的制备方法。本专利技术得到的透镜具有优异的抗裂性能。本专利技术提出的一种高抗裂透镜的制备方法，包括下述步骤：S1、将聚碳酸酯加热至熔融状态，搅拌下加入钨酸钙和棉纤维，继续保温搅拌，冷却，得到改性聚碳酸酯；S2、将改性聚碳酸酯和聚氨酯分别加热至熔化状态后混合均匀，接着置于镜面微细结构的光学辊筒上形成复合膜层，通过镜面微细结构的光学辊筒将复合膜层进行热压制成镜材；S3、将镜材冷却后，对镜材的上下表面进行覆膜，修边，得到高抗裂透镜。优选地，S1中，聚碳酸酯、钨酸钙和棉纤维的重量比为1：0.2-1.5：0.3-1.4。优选地，S1中，聚碳酸酯、钨...
【技术保护点】
1.一种高抗裂透镜的制备方法，其特征在于，包括下述步骤：S1、将聚碳酸酯加热至熔融状态，搅拌下加入钨酸钙和棉纤维，继续保温搅拌，冷却，得到改性聚碳酸酯；S2、将改性聚碳酸酯和聚氨酯分别加热至熔化状态后混合均匀，接着置于镜面微细结构的光学辊筒上形成复合膜层，通过镜面微细结构的光学辊筒将复合膜层进行热压制成镜材；S3、将镜材冷却后，对镜材的上下表面进行覆膜，修边，得到高抗裂透镜。
【技术特征摘要】
1.一种高抗裂透镜的制备方法，其特征在于，包括下述步骤：S1、将聚碳酸酯加热至熔融状态，搅拌下加入钨酸钙和棉纤维，继续保温搅拌，冷却，得到改性聚碳酸酯；S2、将改性聚碳酸酯和聚氨酯分别加热至熔化状态后混合均匀，接着置于镜面微细结构的光学辊筒上形成复合膜层，通过镜面微细结构的光学辊筒将复合膜层进行热压制成镜材；S3、将镜材冷却后，对镜材的上下表面进行覆膜，修边，得到高抗裂透镜。2.根据权利要求1所述高抗裂透镜的制备方法，其特征在于，S1中，聚碳酸酯、钨酸钙和棉纤维的重量比为1：0.2-1.5：0.3-1.4。3.根据权利要求2所述高抗裂透镜的制备方法，其特征在于，S1中，聚碳酸...
【专利技术属性】
技术研发人员：欧阳胜明，
申请(专利权)人：望江县天长光学仪器有限公司，
类型：发明
国别省市：安徽,34