The present invention discloses a new type of solid electrolyte with controllable photocatalytic properties, which includes: based on the quality of ionic liquid EMITFSI, the EMITFSI is 100wt%, 4-8wt% photocatalytic monomer PEGDA, 1-3wt% photocatalyst HOMPP, 5-10wt% silicon-coated Fe3O4 nanoparticles and 1wt%-3wt% polymer particle PEO. The new solid electrolyte (1) of the invention has simple preparation process and does not need complicated operation process; (2) the effective conductive component is over 80%, and the conductivity is high; (3) with the increase of the preparation magnetic field, the micro-nano structure generated in the solid electrolyte is gradually improved, which makes the conductivity of the material increase, and this characteristic can be used as an effective measure to actively control the conductivity of the electrolyte.
【技术实现步骤摘要】
一种光固化性能可控的新型固体电解质
本专利技术涉及固体电解质，特别涉及一种光固化性能可控的新型固体电解质。
技术介绍
聚合物固体电解质，作为全固态超级电容器良好的电子导电载体而被广泛研究报道，然而电解质的电子导电性与其粘度或聚合物成分的多少直接相关：含聚合物较多的固体电解质具有确定的形状和更好的机械强度，然而原本液体电解液的导电性能会丧失大半，反之，固体电解质不具备确定形状，不能形成稳定的片层状材料应用到超级电容器当中。机械强度和导电性能的选择，一直是设计新型固体电解质材料面临的挑战。为了解决以上所提到的挑战，科研人员往往要选择性能更好、更加昂贵的液体电解液原材料或者引入更复杂的人为干预操作控制聚合物的聚合过程。虽然，这些固体电解质的研发过程中被赋予了很多优良的物理特性，然而固体电解质的导电率问题仍未获得实质性的解决，其制备过程也十分繁琐，往往需要高昂的设备投入而且制备耗时很长。因此，现有技术存在问题，本专利技术基于此而研发。
技术实现思路
针对现有技术存在的问题，本专利技术提供一种光固化性能可控的新型固体电解质。为实现上述目的，本专利技术的技术方案如下：一种光固化性...
【技术保护点】
1.一种光固化性能可控的新型固体电解质，其特征在于，包括：以离子液体EMITFSI的质量为基准，即记EMITFSI为100wt％、4～8wt％光固化单体PEGDA、1～3wt％光固化催化剂HOMPP、5～10wt％硅包覆Fe3O4纳米颗粒、1wt％～3wt％聚合物颗粒PEO。
【技术特征摘要】
1.一种光固化性能可控的新型固体电解质，其特征在于，包括：以离子液体EMITFSI的质量为基准，即记EMITFSI为100wt％、4～8wt％光固化单体PEGDA、1～3wt％光固化催化剂HOMPP、5～10wt％硅包覆Fe3O4纳米颗粒、1wt％～3wt％聚合物颗粒P...
【专利技术属性】
技术研发人员：彭刚柔，
申请(专利权)人：广东天劲新能源科技股份有限公司，
类型：发明
国别省市：广东,44