The invention relates to a polyvinyl chloride material formulation, which consists of the following raw materials: resin powder 50 70 parts, heavy calcium powder 25 28 parts, calcium stearate 12 15 parts, zinc oxide 2 3 parts, hexamethylphosphatidyl triamide 1 2 parts, paraffin 0.4 0.5 parts, stearic acid 0.3 0.4 parts, polyester wax 0.25 0.3 parts, ethylene bis fatty acid amide 0.5 8 parts, dioctyl ester 0.7 parts. Di-n-octyltin acid 0.5 1 portion. The beneficial effect of the invention is that the addition of hexamethylphosphatidyl triamide can not only greatly improve the antioxidant performance of PVC pipe, but also has high surface finish, and has low ratio, which is suitable for popularization and application.
【技术实现步骤摘要】
聚氯乙烯材料配方
本专利技术涉及材料领域，具体涉及一种聚氯乙烯材料配方。
技术介绍
PVC材料的软管物美价廉，是目前公认也是应用最多的户外用水管材料，但现有的PVC软管材料制成的软管存在一些缺陷，比如说在户外长期风吹日晒，老化比较快，目前克服该缺陷的办法是添加抗氧化剂跟紫外线吸收剂，但添加的物质比较昂贵，致使PVC软管生产成本较高。
技术实现思路
针对现有技术的不足，本专利技术所要解决的技术问题是，提供一种可以大大提高PVC管材的抗氧化性能，而且成比较低的聚氯乙烯材料配方。本专利技术的具体技术方案如下：一种聚氯乙烯材料配方，由以下重量份数的原料组成：树脂粉50-70份、重碳钙粉25-28份、硬脂酸钙12-15份、氧化锌2-3份、六甲基磷酰三胺1-2份、石蜡0.4-0.5份、硬脂酸0.3-0.4份、聚酯蜡0.25-0.3份、乙撑双脂肪酸酰胺0.5-0.8份、二辛脂0.7-1份；马来酸二正辛基锡0.5-1份。优选的，所述的聚氯乙烯材料配方由以下重量份数的原料组成：树脂粉60份、重碳钙粉27份、硬脂酸钙13份、氧化锌2份、六甲基磷酰三胺2份、石蜡0.4份、硬脂酸0.4份、聚酯蜡0.25份、乙撑双脂肪酸酰胺0.6份、二辛脂0.8份；马来酸二正辛基锡0.8份。本专利技术的有益效果：添加的六甲基磷酰三胺，不但可以大大提高PVC管材的抗氧化性能，表面光洁度高；而且成比较低，适合推广应用。具体实施方式以下结合具体实施例进一步说明本专利技术。实施例1一种聚氯乙烯材料配方由以下重量份数的原料组成：树脂粉60份、重碳钙粉27份、硬脂酸钙13份、氧化锌2份、六甲基磷酰三胺2份、石蜡0...
【技术保护点】
1.一种聚氯乙烯材料配方，其特征在于，由以下重量份数的原料组成：树脂粉50‑70份、重碳钙粉25‑28份、硬脂酸钙12‑15份、氧化锌2‑3份、六甲基磷酰三胺1‑2份、石蜡0.4‑0.5份、硬脂酸0.3‑0.4份、聚酯蜡0.25‑0.3份、乙撑双脂肪酸酰胺0.5‑0.8份、二辛脂0.7‑1份；马来酸二正辛基锡0.5‑1份。
【技术特征摘要】
1.一种聚氯乙烯材料配方，其特征在于，由以下重量份数的原料组成：树脂粉50-70份、重碳钙粉25-28份、硬脂酸钙12-15份、氧化锌2-3份、六甲基磷酰三胺1-2份、石蜡0.4-0.5份、硬脂酸0.3-0.4份、聚酯蜡0.25-0.3份、乙撑双脂肪酸酰胺0.5-0.8份、二辛脂0.7-1份；马来...