The invention discloses a wood plastic PVC foamboard, comprising the following components: PVC 50 100; calcium powder 30 80; AC yellow foaming agent 0.2 0.5; ACyellow foaming agent 0.2 0.5; NC white foaming agent 1 1.5; NCwhite foaming agent 1 1 1 1 1 1.1.5; foaming regulator 5 10; stabilizer 3 8209 5; plasticizer 0.1 8209 plasticizer 0.1 8209 0.5; plasticizer 0.1 anti-impact modifier 1 8209; 5; internal lubricant 0.5 8209 9; internal lubricant 0 5 lubricant 0.5 8209 9; external lubricant 0.5 By weight. Plan. The invention adds wood flour to the formula of PVC foam board to make the produced wood-plastic PVC foam board have high hardness, high strength, good thermoplasticity and high cost performance. It not only meets the market demand, but also reduces the cost.
【技术实现步骤摘要】
一种木塑PVC发泡板
本专利技术涉及一种发泡板，具体涉及一种木塑PVC发泡板。
技术介绍
PVC发泡板又称为雪弗板和安迪板，其化学成分是聚氯乙烯，和传统木质材料相比，具有以下优点：防水、阻燃、耐酸碱、防蛀、质轻、保温、隔音、易加工、可塑性强，因此被广泛用于加装建筑装修材料，市场需求量很大。但目前市场上，PVC发泡板具有硬度和强度低、易损坏、使用年限较短等不足。
技术实现思路
专利技术目的：本专利技术目的在于针对现有技术的不足，提供一种硬度大、强度大、热塑性好、性价比高的木塑PVC发泡板。技术方案：本专利技术所述的木塑PVC发泡板，包括如下组分：SG-5型聚氯乙烯50-100份；钙粉30-80份；AC黄发泡剂0.2-0.5份；NC白发泡剂1-1.5份；发泡调节剂5-10份；稳定剂3-5份；增塑剂0.1-0.5份；抗冲击改性剂1-5份；内润滑剂0.5-1份；外润滑剂0.5-2份；木粉20-40份；以重量份数计。优选地，所述的木塑PVC发泡板，包括如下组分：SG-5型聚氯乙烯75份；钙粉50份；AC黄发泡剂0.4份；NC白发泡剂1.1份；发泡调节剂7.5份；稳定剂3.4份；增塑剂0.25份；抗冲击改性剂2份；内润滑剂0.7份；外润滑剂0.9份；木粉25份；以重量份数计。优选地，所述的木塑PVC发泡板，包括如下组分：SG-5型聚氯乙烯75份；钙粉50份；AC黄发泡剂0.3份；NC白发泡剂1.1份；发泡调节剂8份；稳定剂3.6份；增塑剂0.28份；抗冲击改性剂3份；内润滑剂0.8份；外润滑剂0.8份；木粉28份；以重量份数计。有益效果：本专利技术通过在PVC发泡板配方中...
【技术保护点】
1.一种木塑PVC发泡板，其特征在于，包括如下组分：聚氯乙烯50‑100份；钙粉30‑80份；AC黄发泡剂0.2‑0.5份；NC白发泡剂1‑1.5份；发泡调节剂5‑10份；稳定剂3‑5份；增塑剂0.1‑0.5份；抗冲击改性剂1‑5份；内润滑剂0.5‑1份；外润滑剂0.5‑2份；木粉20‑40份；以重量份数计。
【技术特征摘要】
1.一种木塑PVC发泡板，其特征在于，包括如下组分：聚氯乙烯50-100份；钙粉30-80份；AC黄发泡剂0.2-0.5份；NC白发泡剂1-1.5份；发泡调节剂5-10份；稳定剂3-5份；增塑剂0.1-0.5份；抗冲击改性剂1-5份；内润滑剂0.5-1份；外润滑剂0.5-2份；木粉20-40份；以重量份数计。2.根据权利要求1所述的木塑PVC发泡板，其特征在于，包括如下组分：聚氯乙烯75份；钙粉50份；AC黄发泡剂0.4份...