一种弯曲变形的钢化玻璃的处理方法技术

本发明专利技术公开了一种弯曲变形的钢化玻璃的处理方法，包括如下步骤：S1.提供弯曲变形的钢化玻璃；S2.清洗所述钢化玻璃；S3.采用酸性溶液浸泡处理所述钢化玻璃，去掉钢化玻璃表面的钢化层；S4.对钢化玻璃的表面进行抛光处理。本发明专利技术中采用酸性溶液浸泡处理所述钢化玻璃，去掉钢化玻璃表面的钢化层，释放应力，使得钢化玻璃两面的应力达到平衡，经过处理后的钢化玻璃可以重新进行切割、钢化等处理，使得弯曲变形的钢化玻璃不良品实现再利用，节省成本。

A Treatment Method for Flexural Deformation of Toughened Glass

The invention discloses a method for treating toughened glass with bending deformation, which includes the following steps: S1. Providing toughened glass with bending deformation; S2. Cleaning the toughened glass; S3. Soaking the toughened glass with acid solution to remove the toughened layer on the surface of the toughened glass; and S4. Polishing the surface of the toughened glass. In the invention, the toughened glass is treated by acid solution immersion, the toughened layer on the surface of the toughened glass is removed, the stress is released, and the stress on both sides of the toughened glass is balanced. The treated toughened glass can be re-cut and tempered, so that the defective products of the bended toughened glass can be reused and the cost is saved.

【技术实现步骤摘要】
一种弯曲变形的钢化玻璃的处理方法
本专利技术涉及了玻璃制品
，特别是涉及了一种弯曲变形的钢化玻璃的处理方法。
技术介绍
钢化玻璃属于安全玻璃。钢化玻璃其实是一种预应力玻璃，为提高玻璃的强度，通常使用化学或物理的方法，在玻璃表面形成压应力，玻璃承受外力时首先抵消表层应力，从而提高了承载能力，增强玻璃自身抗风压性，寒暑性，冲击性等。这么玻璃破裂时没有尖边，安全性较好。在钢化玻璃的制备中，由于钢化、抛光等过程控制不好，玻璃两面的钢化程度不一致，因此会导致两面存在应力差，导致成形的钢化玻璃弯曲变形，若弯曲变形超过标准值，则该钢化玻璃没有办法再使用，造成资源浪费，如何安全有效地处理弯曲变形的钢化玻璃一直是行业难题。
技术实现思路
为了弥补已有技术的缺陷，本专利技术提供一种弯曲变形的钢化玻璃的处理方法。本专利技术所要解决的技术问题通过以下技术方案予以实现：一种弯曲变形的钢化玻璃的处理方法，包括如下步骤：S1.提供弯曲变形的钢化玻璃；S2.清洗所述钢化玻璃；S3.采用酸性溶液浸泡处理所述钢化玻璃，去掉钢化玻璃表面的钢化层；S4.对钢化玻璃的表面进行抛光处理。进一步地，步骤S4之后还包括：对钢化玻本文档来自技高网...

【技术保护点】
1.一种弯曲变形的钢化玻璃的处理方法，包括如下步骤：S1.提供弯曲变形的钢化玻璃；S2.清洗所述钢化玻璃；S3.采用酸性溶液浸泡处理所述钢化玻璃，去掉钢化玻璃表面的钢化层；S4.对钢化玻璃的表面进行抛光处理。

【技术特征摘要】
1.一种弯曲变形的钢化玻璃的处理方法，包括如下步骤：S1.提供弯曲变形的钢化玻璃；S2.清洗所述钢化玻璃；S3.采用酸性溶液浸泡处理所述钢化玻璃，去掉钢化玻璃表面的钢化层；S4.对钢化玻璃的表面进行抛光处理。2.如权利要求1所述的处理方...