螺栓生产工艺制造技术

本发明专利技术涉及螺栓生产工艺，其步骤依次为退火、除锈、抽线、成型、辗牙、热处理、表面处理。退火步骤依次为进料、升温、保温、降温。除锈步骤为：酸洗、清水洗、草酸洗、中和洗。热处理步骤依次为：高温回火、淬火、回火。相对于现有技术，本发明专利技术加工工艺简单，并且产品的成品率大大提高，而且生产效率提高，进一步节省了原料，降低了生产成本。

Bolt Production Technology

The invention relates to the production process of bolts, whose steps are annealing, rust removal, wire drawing, forming, tooth rolling, heat treatment and surface treatment in turn. The annealing steps are feeding, heating, holding and cooling in turn. The rust removal steps are: pickling, water washing, oxalic acid washing, neutralization washing. The heat treatment steps are high temperature tempering, quenching and tempering. Compared with the existing technology, the process of the invention is simple, and the yield of the product is greatly improved, and the production efficiency is improved, the raw materials are further saved, and the production cost is reduced.

【技术实现步骤摘要】
螺栓生产工艺
本专利技术涉及一种螺栓生产方法。
技术介绍
螺栓是机械行业中中常用的紧固件，目前的加工方式一般为车削成型，但是该方式生产的强度难以保证，经过出现杆部断裂等问题，严重影响来的正常的生产和设备的正常使用，因此迫切的需要一种新的螺栓生产方法来解决上述技术问题。
技术实现思路
本专利技术正是针对现有技术中存在的技术问题，提供一种可以保证螺栓强度以及保证螺栓质量的螺栓生产工艺。为了实现上述目的，本专利技术的技术方案如下：螺栓生产工艺，其特征在于，所述工艺依次包括以下步骤，退火、除锈、抽线、成型、辗牙、热处理、表面处理。作为本专利技术的一种改进，所述退火步骤如下，进料：将需要处理的产品吊放进退火炉内，升温：将炉内温度缓慢，约5-6小时升至规定温度；保温：对材质进行2-3.5小时保温；降温：将炉内温度缓慢降至500℃以下，然后随炉冷却至常温。作为本专利技术的一种改进，所述除锈步骤如下：酸洗：将整个盘元分别浸入常温、浓度为20-25％的盐酸槽5-15分钟；清水洗：清除线材表面的盐酸腐蚀产物；草酸洗：增加金属的活性，以使下一工序生成的皮膜更为致密。中和洗：用中和剂中和线材表面残留的酸液。作为本文档来自技高网...

【技术保护点】
1.螺栓生产工艺，其特征在于，所述工艺依次包括以下步骤，退火、除锈、抽线、成型、辗牙、热处理、表面处理。

【技术特征摘要】
1.螺栓生产工艺，其特征在于，所述工艺依次包括以下步骤，退火、除锈、抽线、成型、辗牙、热处理、表面处理。2.根据权利要求1所述的螺栓生产工艺，其特征在于，所述退火步骤依次如下，进料：将需要处理的产品吊放进退火炉内，升温：将炉内温度缓慢，约5-6小时升至规定温度；保温：对材质进行2-3.5小时保温；降温：将炉内温度缓慢降至500℃以下，然后随炉冷却至常温。3.根据权利要求1所述的螺栓生产工艺，其...

【专利技术属性】
技术研发人员：韩董群，
申请(专利权)人：嘉兴市巴斯夫塑业有限公司，
类型：发明
国别省市：浙江,33