一种轻质蛋白石页岩塑料粒子的制作方法技术

本发明专利技术提供一种轻质蛋白石页岩功能塑料粒子的制造方法，一种轻质蛋白石页岩功能塑料粒子的制造方法，其步骤是：(按重量比份)取塑料粒子40‑80份，采用冷冻方法将所述的塑料粒子粉碎60‑100目粉体，然后烘干，含水量控制在小于0.2％，再加入偶联剂5‑10份、分散剂10‑20份；将所有物料放在一起，充分搅拌，放入双螺杆挤出机中，熔融挤出、冷却、切粒。通过该简单的方法即可制造成高品质的轻质蛋白石页岩功能塑料粒子。

A Method of Making Light opal Shale Plastic Particles

The invention provides a method for manufacturing light opal shale functional plastic particles, and a method for manufacturing light opal shale functional plastic particles. The steps are as follows: (according to weight ratio) 40 to 80 plastic particles are taken, the plastic particles are crushed into 60 to 100 mesh by freezing method, then dried, the water content is controlled to be less than 0.2%, and 5 to 10 copies of coupling agent are added. Dispersant 10 20 parts; put all materials together, stir fully, put into twin screw extruder, melt extrusion, cooling, granulation. Through this simple method, high quality light opal shale functional plastic particles can be produced.

【技术实现步骤摘要】
一种轻质蛋白石页岩塑料粒子的制作方法
技术介绍
本专利技术涉及一种功能塑料粒子制造
，特别是涉及一种轻质蛋白石页岩功能塑料粒子的制作方法。
功能塑料粒子，就是将塑料粒子加以改性，也就是将石油化工企业生产出的大批量通用树脂，通过物理的化学的机械的方法，改善或增加其功能，在磁、光、电、耐老化、阻燃、机械性能等方面达到特殊环境条件下使用的塑料功能粒子；其方法：将树脂中加入偶联剂、无机矿物重钙、滑石、云母、硫酸钡、硅土、玻璃微珠、蒙脱土等进行改性，达到所需的功能粒子；这种粒子存在不足之处，将其做成产品比重较大，同体积产品较重；特别是涉及一种具有保健功能的轻质蛋白石页岩功能塑料粒子，目前应还没发现应用和记载。
技术实现思路
针对现有技术的不足，本专利技术提供一种轻质蛋白石页岩塑料粒子的制作方法：其步骤是：(按重量比份)取塑料粒子40-80份，采用冷冻方法将所述的塑料粒子粉碎55-95目粉体，然后烘干，含水量控制在小于0.2％，再加入偶联剂5-10份、分散剂15-20份；将所有物料放在一起，充分搅拌，放入双螺杆挤出机中，熔融挤出、冷却、切粒。进一步地，所述分散剂为PP分子蜡。进一步地，所述分散本文档来自技高网...

【技术保护点】
1.一种轻质蛋白石页岩功能塑料粒子的制造方法，其步骤是：(按重量比份)取塑料粒子40‑80份，采用冷冻方法将所述的塑料粒子粉碎55‑95目粉体，然后烘干，含水量控制在小于0.2％，再加入偶联剂5‑10份、分散剂15‑20份；将所有物料放在一起，充分搅拌，放入双螺杆挤出机中，熔融挤出、冷却、切粒。

【技术特征摘要】
1.一种轻质蛋白石页岩功能塑料粒子的制造方法，其步骤是：(按重量比份)取塑料粒子40-80份，采用冷冻方法将所述的塑料粒子粉碎55-95目粉体，然后烘干，含水量控制在小于0.2％，再加入偶联剂5-10份、分散剂15-20份；将所有物料放在一起，充分搅拌...