The invention belongs to the technical field of water treatment, and in particular provides a red mud adsorbent, a preparation method and application thereof. The present invention takes alkaline red mud as raw material, removes part of free alkali in red mud by washing and precipitation in the process of seawater washing modification, and then improves the content of iron oxide adsorbed in red mud by modifying with ferric chloride solution, thereby improving its adsorptive capacity; the preparation cost of the present invention is low, and the red mud adsorbent obtained by this method has good adsorptive capacity for arsenic and fluorine; Moreover, the adsorption can be directly stacked without subsequent desorption.
【技术实现步骤摘要】
一种赤泥吸附剂及其制备方法和应用
本专利技术属于水处理
，具体涉及一种赤泥吸附剂及其制备方法和应用。
技术介绍
随着生活水平的提高，工业水平的发展，地下水中砷和氟污染问题突出，其中以砷和氟复合污染的情况较为常见，砷和氟联合中毒事件频发，对水质安全和人体健康造成威胁。目前针对水中砷、氟污染的主要去除手段有：电絮凝法、化学药剂絮凝法、膜过滤法和吸附法；其中吸附法以其清洁优势，受到广泛关注。吸附工艺过程包括吸附材料的制备、吸附和吸附后的吸附剂处理；三个方面共同决定着水污染的处理效果和处理成本。现今对吸附工艺投入了大量研究，虽然取得了一定进展，但是现阶段吸附工艺成本较高；并且采用现阶段所研制的吸附剂对水中砷、氟进行吸附后，为了降低原料成本还需对吸附剂进行解吸处理。例如，中国专利CN102139202A公开了一种用于水中砷和氟去除的纤维素基材料，但是该吸附剂的制备工艺复杂，制备过程中需要用到的原料种类较多，且对制备条件要求较高，均导致了水中污染元素吸附工艺成本的提高。
技术实现思路
有鉴于此，本专利技术提供了一种赤泥吸附剂及其制备方法和应用，本专利技术制备得到的赤泥吸附剂...
【技术保护点】
1.一种赤泥吸附剂的制备方法，包括以下步骤：(1)采用海水对赤泥进行水洗改性，得到海水改性赤泥；(2)将所述步骤(1)得到的海水改性赤泥与氯化铁溶液混合，对得到的混合液进行加热改性，得到赤泥吸附剂。
【技术特征摘要】
1.一种赤泥吸附剂的制备方法，包括以下步骤：(1)采用海水对赤泥进行水洗改性，得到海水改性赤泥；(2)将所述步骤(1)得到的海水改性赤泥与氯化铁溶液混合，对得到的混合液进行加热改性，得到赤泥吸附剂。2.根据权利要求1所述的制备方法，其特征在于，所述步骤(1)中海水和赤泥的质量比为(15～40)：1；所述水洗改性的时间为1～2h。3.根据权利要求1所述的制备方法，其特征在于，所述步骤(2)中氯化铁溶液的浓度为0.3～0.8mol/L；所述氯化铁溶液的用量以使所述混合液的pH值为3.0～4.0为准。4.根据权利要求1所述的制备方法，其特征在于，所述步骤(2)中加热改性的温度为20～90℃；所述加热改性的时间以使混合液的pH值稳定在4.0～5.0为准。5.根据权利要求1～4任一项所述的制备方法，其特征在于，所述赤泥为由拜耳法炼铝产生的碱性废物赤泥；所述海水包括以下浓度的阳离子：Ca2+350～6...
【专利技术属性】
技术研发人员：王洪涛，李风亭，张路，亓雪娇，
申请(专利权)人：同济大学，
类型：发明
国别省市：上海,31