The invention discloses a new method for manufacturing microporous permeable film and its application. The permeable particles are obtained by blending and extruding the polyolefin body with instant powders. The permeable particles are heated by a flow casting extruder and fully melted. The melt is extruded into a film shape by a flow casting machine, and then cooled and finalized, solvents or aqueous solutions or steam degassed. Washing, drying and corona treatment are used to manufacture polyolefin permeable membranes with stable micropore, which avoids pinholes in the production process of polyolefin permeable membranes with calcium carbonate system in the prior art when stretching orientation is required.
【技术实现步骤摘要】
一种新型微孔透气膜的制造方法及其应用
本专利技术涉及一种新型微孔透气膜的制造方法及其应用。
技术介绍
透气膜广泛应用于一次性吸收用品中，其起防水透气的作用，让使用者使用过程中防止漏液的同时透气，提高用户的使用舒适度。现有技术中聚烯烃透气膜为碳酸钙体系的透气膜，由于碳酸钙本身跟聚烯烃的相容性差，碳酸钙体系的聚烯烃透气膜存在相分离的问题，且薄膜需要被拉伸取向时容易存在出现针孔等问题，影响聚烯烃透气膜的使用。
技术实现思路
为了克服现有技术的不足，本专利技术提供一种新型微孔透气膜的制造方法及其应用。本专利技术解决其技术问题所采用的技术方案是：一种新型微孔透气膜的制造方法，包括以下步骤，A)所述聚烯烃本体、速溶性粉体按比例经双螺杆挤出机，共混挤出造粒，制得透气粒子；B)所述透气粒子经流延挤出机模头定量挤出成薄膜，熔体温度为100-160℃；C)经拉伸后获得的薄膜经热定型，冷却定型，溶剂或水溶液或蒸汽脱洗、烘干、电晕处理，收卷切边工序形成具有稳定微孔的聚烯烃透气膜。其中：所述聚烯烃本体为透明度高的低密度聚乙烯LDPE、线性低密度聚乙烯LLDPE、高密度聚乙烯HDPE、聚丙烯PP...
【技术保护点】
1.一种新型微孔透气膜的制造方法，其特征在于：包括以下步骤，A)所述聚烯烃本体、速溶性粉体按比例经双螺杆挤出机，共混挤出造粒，制得透气粒子；B)所述透气粒子经流延挤出机模头定量挤出成薄膜，熔体温度为100‑160℃；C)经拉伸后获得的薄膜经热定型，冷却定型，溶剂或水溶液或蒸汽脱洗、烘干、电晕处理，收卷切边工序形成具有稳定微孔的聚烯烃透气膜。
【技术特征摘要】
1.一种新型微孔透气膜的制造方法，其特征在于：包括以下步骤，A)所述聚烯烃本体、速溶性粉体按比例经双螺杆挤出机，共混挤出造粒，制得透气粒子；B)所述透气粒子经流延挤出机模头定量挤出成薄膜，熔体温度为100-160℃；C)经拉伸后获得的薄膜经热定型，冷却定型，溶剂或水溶液或蒸汽脱洗、烘干、电晕处理，收卷切边工序形成具有稳定微孔的聚烯烃透气膜。2.根据权利要求1所述一种新型微孔透气膜的制造方法，其特征在于：所述聚烯烃本体为透明度高的低密度聚乙烯LDPE、线性低密度聚乙烯LLDPE、高密度聚乙烯HDPE、聚丙烯PP的其中一种或多种组成。3.根据权利要求1所述一种新型微孔透气膜的制造方法，其特征在于：所述速溶性粉体为速溶性聚合物粉体、速溶性植物粉体的其中一种或两种组成。4.根据权利要求1所述一种新型微孔透气膜的制造方法，其特征在于：所述速溶性粉体与聚烯烃本体的比例为100:100～100:70。5.根据权利要求1所述一种新型微孔...
【专利技术属性】
技术研发人员：徐水坤，
申请(专利权)人：广东玛喜儿卫生用品有限公司，
类型：发明
国别省市：广东,44