The invention is a method for measuring the spacing of light filaments in laser filament filling special welding technology. The invention can accurately measure the optimum spacing of light filaments DAL required for welding seam forming through experiments. The wire spacing DAL refers to the distance between the laser spot center and the contact point between the wire diameter center and the workpiece surface. When the wire spacing is 0 mm, although the front of the weld is well formed, the width of the back is significantly different in different regions, which is not conducive to the uniformity of the weld. When the welding speed is 4.2m/min, the spacing between the wires should be strictly controlled in the range of + 0.8 to + 1.4. When the welding speed is 3.0m/min, the spacing between the wires should be controlled in the range of + 0.4 to + 2m. If the spacing between the wires is too large, it will not melt completely under the action of plasma cloud, resulting in partial undercut of the weld seam. Defects such as welding leak and wire standing.
【技术实现步骤摘要】
一种测量光丝间距的方法
本专利技术涉IC装备制造业激光填丝特种焊接技术，在激光填丝焊接技术中心，光丝间距对焊缝成形影响较大，属于重要焊接变素。本专利技术阐述了一种测量光丝间距的方法。
技术介绍
在激光填丝焊接铝合金技术中，光丝间距对铝合金激光填丝焊接成形影响较大，但是常常因为测量工具不专业以及测量方法不正确引起测量误差，导致焊缝成形不一致的问题。精确测量光丝间距DAL便于在生产中控制变量，保证焊接产品质量一致性。通过本专利技术，可以通过实验准确测量出焊缝成形需要的最佳光丝间距DAL。
技术实现思路
本专利技术目的是提供一种一种测量光丝间距的方法。本专利技术采用的技术方案是：一种测量光丝间距的方法，利用带有刻度的标尺，最小刻度0.2mm，通过CCD放大镜在标尺上读取数值，通过换算，获得激光填丝间距DAL，换算公式如下：DAL＝L-d/2公式(1)公式(1)中，DAL是光丝间距，L是标尺上的读数，d是焊丝直径。标尺总长40mm，宽度10mm，最小刻度为0.2mm，光丝间距精确度0.2mm。测量结果如下：当焊接速率为4.2m/min时，光丝间距严格控制在+0.8～+1.4范...
【技术保护点】
1.一种测量光丝间距的方法，其特征在于：利用带有刻度的标尺，最小刻度0.2mm，通过CCD放大镜在标尺上读取数值，通过换算，获得激光填丝间距DAL，换算公式如下：DAL＝L‑d/2 公式(1)公式(1)中，DAL是光丝间距，L是标尺上的读数，d是焊丝直径。
【技术特征摘要】
1.一种测量光丝间距的方法，其特征在于：利用带有刻度的标尺，最小刻度0.2mm，通过CCD放大镜在标尺上读取数值，通过换算，获得激光填丝间距DAL，换算公式如下：DAL＝L-d/2公式(1)公式(1)中，DAL是光丝间距，L是标尺上的读数，d是焊丝直径。2.按照权利要求1所述一种测量光丝间距的方法，其特征在于：标尺总长40mm，宽度10...
【专利技术属性】
技术研发人员：李文明，李生智，谯永鹏，张维，
申请(专利权)人：沈阳富创精密设备有限公司，
类型：发明
国别省市：辽宁,21