侧墙搅拌摩擦焊控制变形工艺制造技术

本发明专利技术公开了一种侧墙搅拌摩擦焊控制变形工艺，通过改变焊接顺序，即采用正面部分顺序焊接、反面顺序焊接及正面剩余焊缝焊接，可使焊接变形大幅减小，使焊后整体平面度达到要求，消除或降低了调修任务量；避免了对焊缝的二次加热，不仅节约了工时，也提高了焊接生产效率，保证了产品性能。

Controlled Deformation Technology of Side Wall Friction Stir Welding

The invention discloses a side wall friction stir welding technology for controlling deformation. By changing the welding sequence, i.e., adopting the front part sequential welding, the reverse sequence welding and the front residual weld welding, the welding deformation can be greatly reduced, the overall flatness after welding can meet the requirements, and the adjustment task can be eliminated or reduced. The second heating of the weld not only saves the working hours, but also improves the welding production efficiency and ensures the product performance.

【技术实现步骤摘要】
侧墙搅拌摩擦焊控制变形工艺
本专利技术属于铝合金焊接领域，涉及一种侧墙搅拌摩擦焊控制变形工艺。
技术介绍
采用搅拌摩擦焊焊接的产品与采用熔化焊焊接的产品相比，虽然变形较小，但仍然不够理想，且搅拌摩擦焊焊接过程中无法预制反变形，只能正常装夹焊接后进行调修矫形，不仅会占用大量工时，且调修过程是对焊缝的二次加热，会对力学性能产生一定影响。
技术实现思路
有鉴于此，本专利技术的目的在于提供一种侧墙搅拌摩擦焊控制变形工艺，以减小焊接变形，同时提高焊接生产效率。为达到上述目的，本专利技术提供如下技术方案：一种侧墙搅拌摩擦焊控制变形工艺，主要包括以下步骤：(1)将几块侧墙板型材进行焊前清理，依次组对并点固成侧墙整体；(2)正面焊接：除中间焊缝外，由侧墙Ⅱ侧向Ⅰ侧方向依次焊接正面的几条焊缝；(3)反面焊接：由侧墙Ⅱ侧向Ⅰ侧方向依次焊接反面的几条焊缝；(4)正面焊接：焊接侧墙正面剩余的中间焊缝；(5)焊后冷却至室温，松开夹具。进一步，采用ESABGantry4U搅拌摩擦焊接机器人对侧墙板型材进行焊接。本专利技术的有益效果在于：通过改变焊接顺序，可使焊接变形大幅减小，使焊后整体平面度达到要求，即使实际生产中本文档来自技高网...

【技术保护点】
1.一种侧墙搅拌摩擦焊控制变形工艺，其特征在于主要包括以下步骤：(1)将几块侧墙板型材进行焊前清理，依次组对并点固成侧墙整体；(2)正面焊接：除中间焊缝外，由侧墙Ⅱ侧向Ⅰ侧方向依次焊接正面的几条焊缝；(3)反面焊接：由侧墙Ⅱ侧向Ⅰ侧方向依次焊接反面的几条焊缝；(4)正面焊接：焊接侧墙正面剩余的中间焊缝；(5)焊后冷却至室温，松开夹具。

【技术特征摘要】
1.一种侧墙搅拌摩擦焊控制变形工艺，其特征在于主要包括以下步骤：(1)将几块侧墙板型材进行焊前清理，依次组对并点固成侧墙整体；(2)正面焊接：除中间焊缝外，由侧墙Ⅱ侧向Ⅰ侧方向依次焊接正面的几条焊缝；(3)反面焊接：由侧墙Ⅱ侧向Ⅰ侧方...

【专利技术属性】
技术研发人员：李英奇，高雨，徐伍刚，杨兴亮，
申请(专利权)人：辽宁忠旺铝合金精深加工有限公司，
类型：发明
国别省市：辽宁,21