Wear-resistant surfacing process, which involves a welding process, includes: first, preparation before welding, selection of appropriate welding rods and wear-resistant fusion welding metal; second, removal of impurities on the surface to be surfacing until metal gloss; third, preheating and layer temperature control before surfacing, wrapping the pipeline around the welding site before welding, uniform heating. Pipeline; 4. Slow cooling after welding, continuous welding of preheated pipeline, without interruption, always control the temperature of pipeline, cover pipeline after surfacing, heat preservation and slow cooling, complete surfacing welding. After repeated tests, the process parameters were adjusted, and the welding cracks were avoided by preheating before welding and cooling slowly after welding.
【技术实现步骤摘要】
耐磨堆焊工艺
本专利技术涉及一种焊接工艺，特别涉及一种耐磨堆焊工艺。
技术介绍
在锅炉产品喷水减温器的两端堆焊耐磨合金，喷水减温器螺钉与筒身摩擦，防止对筒身造成损害，影响喷水减温器的使用寿命，但是，现有焊接过程中容易开裂，如图1所示，影响产品质量，不利于喷水减温器的长期使用。
技术实现思路
本专利技术为克服现有技术不足，提供一种耐磨堆焊工艺。该工艺经过反复试验，调整工艺参数，通过焊前预热、焊后缓冷的措施，避免焊接裂纹出现。本专利技术的技术方案是：耐磨堆焊工艺，包括：一、焊前准备，选择合适的焊条和耐磨熔焊金属；二、清除待堆焊表面的杂质，直至露出金属光泽；三、堆焊前预热及层温控制，焊前对焊接部位的管道环向进行包裹，均匀加热管道，预热至250℃以上；四、焊后缓冷，对预热后的管道连续施焊，不得间断，始终控制管道温度大于250℃，堆焊后覆盖管道，保温缓冷，完成堆焊接。进一步地，在低合金耐热钢12Cr1MoVG上，堆焊耐磨熔焊金属采用EDCrNi-A-15(D547)。本专利技术的有益效果是：本专利技术工艺简单，可靠，通过焊前预热、焊后缓冷的措施，避免了焊接裂纹出现，经渗透检测无...
【技术保护点】
1.耐磨堆焊工艺，其特征在于：它包括：一、焊前准备，选择合适的焊条和耐磨熔焊金属；二、清除待堆焊表面的杂质，直至露出金属光泽；三、堆焊前预热及层温控制，焊前对焊接部位的管道环向进行包裹，均匀加热管道，预热至250℃以上；四、焊后缓冷，对预热后的管道连续施焊，不得间断，始终控制管道温度大于250℃，堆焊后覆盖管道，保温缓冷，完成堆焊。
【技术特征摘要】
1.耐磨堆焊工艺，其特征在于：它包括：一、焊前准备，选择合适的焊条和耐磨熔焊金属；二、清除待堆焊表面的杂质，直至露出金属光泽；三、堆焊前预热及层温控制，焊前对焊接部位的管道环向进行包裹，均匀加热管道，预热至250℃以上；四、焊后缓冷，对预热后的管道连续施焊，不得间断，始终控制管道温度大于250℃，堆焊后覆盖管道，保温缓冷，完成堆焊。2.根据权利要求1所述耐磨堆焊工艺，其特征在于：焊前采用履带式加热器对焊接部位的管道环向进行包裹。3.根据权利要求2所述耐磨堆焊工艺，其特...
【专利技术属性】
技术研发人员：赵国洋，赵丹，于鹏飞，刘德余，
申请(专利权)人：哈尔滨哈锅锅炉容器工程有限责任公司，
类型：发明