天然沥青乳化剂制造技术

本发明专利技术涉及工业乳化剂技术领域，尤其是一种天然沥青乳化剂，包括以下质量份的组分：聚乙烯醇3.25~6.8份，去离子水75~105份，戊基酚聚氧乙烯醚0.65~1.25份，庚基酚聚氧乙烯醚0.52~1.45份和柠檬酸0.5~3.5份，利用该配方制得的乳化剂对沥青进行球化处理的益处在于，缩短了分散体系达到稳定的时间，避免了沥青颗粒之间的融并及长大，增大了沥青成球处理时的沥青添加量，提高了沥青的成球效率，为规模化沥青成球处理奠定了基础。

Natural asphalt emulsifier

The invention relates to the technical field of industrial emulsifier, in particular to a natural asphalt emulsifier, which comprises the following components: 3.25-6.8 parts of polyvinyl alcohol, 75-105 parts of deionized water, 0.65-1.25 parts of pentyl phenol polyoxyethylene ether, 0.52-1.45 parts of heptyl phenol polyoxyether and 0.5-3.5 parts of citric acid. The advantage of spheroidizing asphalt with additives is that it shortens the time for dispersing system to reach stability, avoids the coalescence and growth of asphalt particles, increases the asphalt dosage in asphalt spheroidizing treatment, improves the spheroidizing efficiency of asphalt, and lays a foundation for large-scale asphalt spheroidizing treatment.

【技术实现步骤摘要】
天然沥青乳化剂
本专利技术涉及工业乳化剂
，尤其是一种天然沥青乳化剂。
技术介绍
乳化剂是能够改善乳浊液中各种构成相之间的表面张力，使之形成均匀稳定的分散体系或乳浊液的物质。乳化剂是表面活性物质，分子中同时具有亲水基和亲油基，它聚集在油/水界面上，可以降低界面张力和减少形成乳状液所需要的能量，从而提高乳状液的能量，其中，沥青是由不同分子量的碳氢化合物及其非金属衍生物组成的黑褐色复杂混合物，是高黏度有机液体的一种，呈液态，表面呈黑色，可溶于二硫化碳，是一种防水防潮和防腐的有机胶凝材料。现有用于沥青球化处理的乳化剂添加量较小，造成成球效果差，达到体系稳定时间长，不利于大规模生产。
技术实现思路
为了克服现有的上述的不足，本专利技术提供了一种天然沥青乳化剂。本专利技术解决其技术问题所采用的技术方案是：一种天然沥青乳化剂，包括以下质量份的组分：聚乙烯醇3.25~6.8份，去离子水75~105份，戊基酚聚氧乙烯醚0.65~1.25份，庚基酚聚氧乙烯醚0.52~1.45份和柠檬酸0.5~3.5份。进一步的，包括聚乙烯醇3.5~6.5份，去离子水80~100份，戊基酚聚氧乙烯醚0.8~1.2份，本文档来自技高网...

【技术保护点】
1.一种天然沥青乳化剂，其特征是在于，包括以下质量份的组分：聚乙烯醇3.25~6.8份，去离子水75~105份，戊基酚聚氧乙烯醚0.65~1.25份，庚基酚聚氧乙烯醚0.52~1.45份和柠檬酸0.5~3.5份。

【技术特征摘要】
1.一种天然沥青乳化剂，其特征是在于，包括以下质量份的组分：聚乙烯醇3.25~6.8份，去离子水75~105份，戊基酚聚氧乙烯醚0.65~1.25份，庚基酚聚氧乙烯醚0.52~1.45份和柠檬酸0.5~3.5份。2.根据权利要求1所述的天然沥青乳化剂，其特征是，所述聚乙烯...