The invention provides a method for improving the mechanical properties of thermoplastic carbon fiber composite materials, which comprises the following steps: A. uniformly dispersing graphene oxide in water to obtain graphene oxide solution; B. uniformly dispersing carbon fiber in graphene oxide solution obtained in step a to obtain graphene oxide coated carbon fiber by drying. C. Graphite oxide coated carbon fibers and polyphenylene ether were melted and blended to form composite materials. The experimental results show that the polyphenylene sulfide prepared by the method has high mechanical properties, and its tensile strength is 116% and 193% higher than that of the unmodified polyphenylene sulfide, and 13% and 17% higher than that of the carbon fiber modified polyphenylene sulfide, respectively.
【技术实现步骤摘要】
一种提高热塑性碳纤维复合材料力学性能的界面组装结构及方法
本专利技术涉及一种复合材料的制备方法，具体涉及一种提高热塑性碳纤维复合材料力学性能的界面组装结构及方法。
技术介绍
聚苯硫醚英文简写为PPS，是一种新型高性能热塑性树脂，具有机械强度高、耐高温、耐化学药品性、难燃、热稳定性好、电性能优良等优点。为了拓宽其应用范围，会对其强度或者韧性进行改进。目前，通常采用玻璃纤维、碳纤维或芳纶纤维来改性聚苯硫醚，提高其强度。与玻璃纤维、芳纶纤维改性的聚苯硫醚相比，采用碳纤维改性的聚苯硫醚具有更优异的综合性能。但是，由于碳纤维具有化学惰性，而且与大多数树脂基体的界面润湿性差，导致其不能大幅度的提高聚苯硫醚的机械性能，使得聚苯硫醚的应用受到限制。目前有通过界面改性剂来改善聚苯硫醚复合材料机械性能的报道，但是改善效果一般，如，文献《张坤等.界面改性剂对聚苯硫醚/碳纤维复合材料力学和热力学性能的影响[J].塑料工业,2013(1):100-103》公开了以环氧丙酮为界面改性剂，改善聚苯硫醚的力学性能，但是，其拉伸强度仅提高了3.4％，提升幅度并不显著。
技术实现思路
为了解决现有技术的...
【技术保护点】
1.一种提高热塑性碳纤维复合材料力学性能的方法，其特征在于：它包括以下步骤：a、将氧化石墨烯均匀分散在水中，即得氧化石墨烯溶液；b、将碳纤维均匀分散在步骤a所得氧化石墨烯溶液中，干燥，即得氧化石墨烯包覆碳纤维；c、将氧化石墨烯包覆碳纤维与聚苯醚熔融共混后即得复合材料。
【技术特征摘要】
1.一种提高热塑性碳纤维复合材料力学性能的方法，其特征在于：它包括以下步骤：a、将氧化石墨烯均匀分散在水中，即得氧化石墨烯溶液；b、将碳纤维均匀分散在步骤a所得氧化石墨烯溶液中，干燥，即得氧化石墨烯包覆碳纤维；c、将氧化石墨烯包覆碳纤维与聚苯醚熔融共混后即得复合材料。2.根据权利要求1所述的方法，其特征在于：步骤a中，所述氧化石墨烯与水的重量体积比为0.1～1:500g/ml；所述分散为超声分散，分散条件为以频率40kHz超声处理1h。3.根据权利要求1或2所述的方法，其特征在于：步骤b中，所述氧化石墨烯包覆的碳纤维中，氧化石墨烯与碳纤维的重量比为0.1～1:15～40。4.根据权利要求3所述的方法，其特征在于：所述氧化石墨烯与碳纤维的重量比为0.1～1:15。5.根据权利要求1～4任一项所述的方法，其特征在于：步骤b中，所述分散为超声分散，分散条件为以频率20kH...
【专利技术属性】
技术研发人员：邹华维，刘琦，罗维，陈洋，梁梅，
申请(专利权)人：四川大学，
类型：发明
国别省市：四川,51