The invention relates to a self-supporting flexible superhydrophilic titanium oxide film and a preparation method thereof. The self-supporting flexible superhydrophilic titanium oxide film is obtained by coating water-soluble sacrificial layer, flexible substrate and titanium oxide nanosheet stripping solution on the base surface in turn, and removing the water-soluble sacrificial layer with water after drying. The self-supporting flexible superhydrophilic titanium oxide film can be obtained on a large scale by this method. The size and shape of the film can be adjusted arbitrarily. The sticky material can be coated on the back of the film, and the sticky self-supporting flexible superhydrophilic titanium oxide film can be obtained.
【技术实现步骤摘要】
一种自支撑柔性超亲水氧化钛薄膜及其制备方法
本专利技术涉及一种自支撑柔性超亲水氧化钛薄膜的制备方法，具体涉及将高活性二氧化钛纳米片剥离液负载在柔性衬底上，自然干燥得到高吸附性能高催化性能的二氧化钛柔性薄膜的方法。
技术介绍
随着环境污染和能源危机的日益严峻，太阳能作为最有应用前景的清洁能源受到了广泛的关注。二氧化钛作为一种储量丰富而又性能优良的半导体材料，自1972年发现二氧化钛光电极表面持续产氢的现象以来(Fujishima,A.；Honda,K.；Nature238,37-38)，基于二氧化钛的半导体光催化技术受到了极大关注并取得了巨大的进展。氧化钛可以广泛地应用于降解有机污染物、裂解水产氢、抗菌和防污等方面，是解决目前能源短缺和环境污染等问题的一个理想途径。但是，常用的材料氧化钛颗粒，吸附性能较差，吸附速率慢，并且难以回收再利用。因此，改性氧化钛催化剂，设计和开发新工艺以应对日益严重的环境污染问题具有十分重大的意义。近年来，有关无机层状化合物剥离分层制备二维单分子层纳米片(nanosheets)的研究越来越受到研究者的青睐。由层状化合物剥离生成的二维纳米片，...
【技术保护点】
1.一种自支撑柔性超亲水氧化钛薄膜的制备方法，其特征在于，在基底表面依次涂覆水溶性牺牲层、柔性衬底和氧化钛纳米片剥离液，经干燥后用水去掉水溶性牺牲层，得到所述自支撑柔性超亲水氧化钛薄膜。
【技术特征摘要】
1.一种自支撑柔性超亲水氧化钛薄膜的制备方法，其特征在于，在基底表面依次涂覆水溶性牺牲层、柔性衬底和氧化钛纳米片剥离液，经干燥后用水去掉水溶性牺牲层，得到所述自支撑柔性超亲水氧化钛薄膜。2.根据权利要求1所述的制备方法，其特征在于，所述水溶性牺牲层的材料选自聚苯乙烯磺酸钠、丙烯酰胺的聚合物、甲基丙烯酰胺的聚合物、丙烯酰胺和甲基丙烯酰胺的共聚物、丙烯酸和甲基丙烯酰胺的共聚物及其盐、丙烯酸和丙烯酰胺的共聚物及其盐、甲基丙烯酸和甲基丙烯酰胺的共聚物及其盐、甲基丙烯酸与丙烯酰胺的共聚物及其盐、海藻酸、瓜尔胶、羧甲基纤维素、淀粉的钠盐中的至少一种。3.根据权利要求1或2所述的制备方法，其特征在于，所述涂覆方式为旋涂，所述旋涂的参数包括：转数：800～4000rpm；时间10～30秒。4.根据权利要求1-3中任一项所述的制备方法，其特征在于，氧化钛纳米片剥离液的制备方法包括：将层状碱金属钛酸盐和浓度为0.5～2M的酸溶液按照1～40g/L的液固比混合并搅拌，得到...
【专利技术属性】
技术研发人员：黄富强，赵雯丽，
申请(专利权)人：中国科学院上海硅酸盐研究所，
类型：发明
国别省市：上海,31